Abstract:Chitosans with different average molecular weight (1,500-156 kDa) were prepared under optimal conditions based on our previous research by the depolymerization of initial chitosan using hydrogen peroxide, with maintaining the native structure of natural chitosan as principal consideration. Nitrogen and Carbon components of initial chitosan and degraded products were analyzed by BUCHI fully automatic nitrogen determination system and Liquid total organic carbon (TOC) analyzer respectively. Fourier transform infrared (FTIR), 13C nuclear magnetic resonance (13C NMR), X-ray diffraction and circular dichroism (CD) analyses were used to characterize the structure properties of samples. The results indicated that the maximum standard deviations of carbon content and nitrogen content and the degree of deacetylation (DD) of degraded products with the corresponding values of the initial chitosan are 2.4%, 2.3% and 6.9% respectively. Besides, the differentiations of the nitrogen content and DD value of the degraded product with the corresponding values of the initial chitosan are narrowed with the increase in the reaction time. FTIR spectra of resulting products are similar to that of initial chitosan in terms of peak number and position, indicating that there are no other functional groups formed during the degradation. 13C-NMR analyses of initial chitosan and degraded products revealed that the chemical structures of resulting chitosans are not changed to any noticeable extent. X-ray diffraction patterns of initial chitosan and degraded chitosans are alike and show characteristic peaks at 2theta = 10. 4 degrees and 19.8 degrees under the condition that the initial chitosan was disposed as degraded chitosans. Circular dichroism analyses showed that all the samples exhibit a broad negative band located at about 210 nm assigned to n --> pi* electronic transition of the --NH--CO-- chromophore on a glycosidic ring in acidic media, which demonstrated that degraded chitosans maintain their natural conformation in liquid state substantially. All these confirmed that the degraded chtiosans maintain their natural structure and conformation, and the breakage of beta-1,4-glucoside bonds in macromolecule is the basic process under optimal degradation conditions.

Irradiation and sensitizing effects on chitosan degradation

Effect of Glow Discharge Plasma on Surface Modification of Chitosan Film.

Synergetic Degradation of Chitosan with Gamma Radiation and Hydrogen Peroxide

Ultrasound-assisted Synthesis of Chitosan from Fungal Precursors for Biomedical Applications

Effect of 60Co irradiation on the properties of chitosan rod

γ-ray degradation of chitosan to prepare water-soluble oligomers

Radiation Degradation of Chitosan in the Presence of H2o2

Studies on Radiation Degradation of Chitosan in Aqueous Solutions

Study on the Water-Solubility of Chitosan Degraded with Gamma Radiation

Radiation-induced Degradation of Carboxymethylated Chitosan in Aqueous Solution

STUDY ON RADIATION DEGRADATION OF CHITOSAN

Influence of Irradiation Sterilization on Mechanical Properties and Biodegradability of Chitosan Conduits

Radiation-induced Changes in Carboxymethylated Chitosan

[Spectra analyses of chitosans degraded by hydrogen peroxide under optimal conditions]

Glow discharge plasma in water: a green approach to enhancing ability of chitosan for dye removal.

Three Dimensional Chitosan Rods Reinforced by Microwave Irradiation

Preparation of water-soluble oligochitosan by radiation degradation (1):Study on degradation method

Electron-Beam-Induced Grafting of Chitosan onto HDPE/ATZ Composites for Biomedical Applications

Preparation and Characterization of N-succinyl-chitosan

Characterization of nanocomposite film based on chitosan intercalated in clay platelets by electron beam irradiation

Controlling the degradation of covalently cross-linked carboxymethyl chitosan utilizing bimodal molecular weight distribution