Abstract:OBJECTIVE:To improve the poor mechanical strength of porous ceramic scaffold, an integrated method based on three-dimensional (3-D) printing technique is developed to incorporate the controlled double-channel porous structure into the polylactic acid/beta-tricalcium phosphate (PLA/beta-TCP) reinforced composite scaffolds (double-channel composite scaffold) to improve their tissue regeneration capability and the mechanical properties.METHODS:The designed double-channel structure inside the ceramic scaffold consisted of both primary and secondary micropipes, which parallel but un-connected. The set of primary channels was used for cell ingrowth, while the set of secondary channels was used for the PLA perfusion. Integration technology of 3-D printing technique and gel-casting was firstly used to fabricate the double-channel ceramic scaffolds. PLA/beta-TCP composite scaffolds were obtained by the polymer gravity perfusion process to pour PLA solution into the double-channel ceramic scaffolds through the secondary channel set. Microscope, porosity, and mechanical experiments for the standard samples were used to evaluate the composite properties. The ceramic scaffold with only the primary channel (single-channel scaffold) was also prepared as a control.RESULTS:Morphology observation results showed that there was no PLA inside the primary channels of the double-channel composite scaffolds but a dense interface layer between PLA and beta-TCP obviously formed on the inner wall of the secondary channels by the PLA penetration during the perfusion process. Finite element simulation found that the compressive strength of the double-channel composite scaffold was less than that of the single-channel scaffold; however, mechanical tests found that the maximum compressive strength of the double-channel composite scaffold [(21.25 +/- 1.15) MPa] was higher than that of the single-channel scaffold[ (9.76 +/- 0.64) MPa].CONCLUSION:The double-channel composite scaffolds fabricated by 3-D printing technique have controlled complex micropipes and can significantly enhance mechanical properties, which is a promising strategy to solve the contradiction of strength and high-porosity of the ceramic scaffolds for the bone tissue engineering application.

Study on molding technology optimization of preparing porous poly(L-lactic acid)/β-tricalcium phosphate composite scaffold materials

Fabrication and characterization of composite porous scaffold of β-tricalcium phosphate / poly(lactic acid)

Preparation of porous composite scaffold for tissue engineering by means of solvent self-eiffusion process

Improved Biocompatibility of Novel Poly(l-Lactic Acid)/β-Tricalcium Phosphate Scaffolds Prepared by an Organic Solvent-Free Method.

Preparation of PLLA/β-TCP compound porous scaffoldby using NH_4HCO_3 as porogen

Preparation of PLGA/β-TCP Composite Scaffolds with Supercritical CO2 Foaming Technique

In Vitro Characterizations of PLLA/β-TCP Porous Matrix Materials and RMSC-PLLA-β-TCP Composite Scaffolds

Preparation of Poly(l-Lactic Acid)/β-Tricalcium Phosphate Scaffold for Bone Tissue Engineering Without Organic Solvent

[Mechanical Properties of Polylactic Acid/beta-Tricalcium Phosphate Composite Scaffold with Double Channels Based on Three-Dimensional Printing Technique].

Tailor-made poly(L-lactide)/poly(lactide-co-glycolide)/hydroxyapatite composite scaffolds prepared via high-pressure compression molding/salt leaching

Ultraporous Poly(Lactic Acid) Scaffolds With Improved Mechanical Performance Using High-Pressure Molding And Salt Leaching

Study on Composite Bone Tissue Engineering Scaffolds(1)-Properties and Application Evaluation Laminated Composite Scaffolds of Β-Tricalcium Phosphate/poly[l-Lactic Acid]

Matching ratio of beta tricalcium phosphate/calcium polyphosphate fiber/polylactic acid composite scaffolds for cartilage tissue engineering

Preparation of Porous Poly(Lactic Acid)/Tricalcium Phosphate Composite Scaffolds for Tissue Engineering

Development of Strong and Tough beta-TCP/PCL Composite Scaffolds with Interconnected Porosity by Digital Light Processing and Partial Infiltration

Preparation and performance of poly (vinyl alcohol)/polylactic acid/hydroxyapatite composite scaffolds based on 3D printing

Degradation Of Surface Modified Beta-Tcp/Plla Porous Scaffold In Vitro

Preparation and Characterization of Porous β-TCP/PLLA Composites with High β-TCP Content

PLA/TCP Porous Scaffolds for Tissue Engineering Fabricated by Repeatedly Cycling Extraction with Supercritical CO2

Preparation of poly(lactic-co-glycolic acid)/calcium phosphate cement macroporous composite scaffold

Surface Modification of Biodegradable Polymer/TCP Scaffolds and Related Research