Abstract:Introduction Efficiency improvements in flexible DSSCs are expected by employing tailor-made ZnO. We have developed a method to quickly crystallize ZnO by microwave assisted hydrothermal reactions. Structures of these nanocrystals for shapes and sizes, as well as preferentially exposed crystal facets, could significantly influence key parameters such as dye adsorption capability and electron transporting property. Experiment Microwave radiation to aqueous solution containing Zn(CH3COO)2 and structure directing agents (SDAs) such as triethanolamine (TEOA) and 1,2,4,5benzenetetracarboxylic acid (BTCA) with controlled pH by addition of KOH resulted in formation of ZnO. The precipitates were centrifuged, washed and dried in an oven for 12h. Dye adsorption capability was estimated from the amount of D149 dye at saturation after stirring ZnO powder added to D149 solution for 24h. Result and Discussion Well crystallized ZnO but totally different morphology was obtained by using TEOA or BTCA (Fig. 1). Use of TEOA resulted in nanoparticles with hexagonal and bipyramidal (HBP) shape in about 50 to 100 nm size. TEM observation combined with SAED confirmed that the axis connecting two tips of HBP corresponds to the caxis of ZnO. While the rectangular sides in 6-fold symmetry obviously correspond to (100), the triangular facets could possibly be (101), (102) or (103). The angle between ridges and the horizontal line of HBP fell in the range between 38 and 41 from SEM images, so that the triangle is most likely (102) with its occupancy to the total surface area of ca. 84%. On the other hand, the use of BTCA resulted in formation of nano-sheet (NS) ZnO. TEM, SAED and lattice images of NS identified that the mainly exposed facets are of the (100) planes of ZnO. Surface area and D149 adsorption capability were checked for the synthesized ZnO in HBP and NS shapes in comparison with a commercial ZnO. Large difference was found for the area occupied by a D149 molecule as 2.4 (commercial), 0.99 (HBP) and 0.59 (NS) nm, indicating differences of dye adsorption stability for different facets. Their differences in DSSC properties are also studied and discussed. Fig. 1 SEM pictures and imagination structures of differently ZnO nanoparticles.

The Fabrication of an Upright-Standing Zinc Oxide Nanosheet for Use in Dye-Sensitized Solar Cells

A Facile Self-assembly Synthesis of Hexagonal ZnO Nanosheet Films and Their Photoelectrochemical Properties

Fabrication of Hierarchically Assembled Microspheres Consisting of Nanoporous ZnO Nanosheets for High-Efficiency Dye-Sensitized Solar Cells

ZnO nanotube-based dye-sensitized solar cell and its application in self-powered devices.

Nanorod-Nanosheet Hierarchically Structured Zno Crystals on Zinc Foil As Flexible Photoanodes for Dye-Sensitized Solar Cells

Metal-free Organic Dye Sensitized Solar Cell Based on Perpendicular Zinc Oxide Nanosheet Thick Films with High Conversion Efficiency.

In Situ Growth of Zinc Oxide Nanoribbons Within the Interstices of a Zinc Stannate Nanoplates Network on Compacted Woven Metal Wires and Their Enhanced Solar Energy Application

Facile Construction of Nanofibrous Zno Photoelectrode for Dye-Sensitized Solar Cell Applications

Porous ZnO Nanosheet Arrays Constructed on Weaved Metal Wire for Flexible Dye-Sensitized Solar Cells.

Microwave Synthesis of ZnO Nano Crystals for Dye-sensitized Solar Cells

Structural improvement of ZnO electrodes through solution-processed routes for enhancing open-circuit voltage in dye-sensitized solar cells

Facile synthesis of ZnO nanocrystals via a solid state reaction for high performance plastic dye-sensitized solar cells

Fabrication of dye-sensitized solar cells with ZnO nanorods as photoanode and natural dye extract as sensitizer

Zinc Oxide Nanostructure Fabricated In Anodic Alumina Oxide Template By Sol-Gel Method

Flexible solar-cell from zinc oxide nanocrystalline sheets self-assembled by an in-situ electrodeposition process

ZnO Nanocones with High-Index {101̅1} Facets for Enhanced Energy Conversion Efficiency of Dye-Sensitized Solar Cells

In-situ Formation of Dispersed ZnO Nanoparticles in Mesoporous Carbon Counter Electrode for Efficient Dye-Sensitized Solar Cells

Fabrication of ZnO nanostructures sensitized with CdS quantum dots for photovoltaic application using a convenient solution method

Controllable Preparation of 2D and 3D ZnO Micro-Nanostructures and Their Photoelectric Conversion Efficiency

Hydrothermal Preparation and Characterization of ZnO with Various Morphologies for Dye-Sensitized Solar Cells

Electrochemical synthesis of a double‐layer film of ZnO nanosheets/nanoparticles and its application for dye‐sensitized solar cells