Coating Thick MgB 2 Layer on Stainless Steel Substrate
Chinping Chen,Qingrong Feng,Zizhao Gan,Guangcheng Xiong,Jun Xu,Yufei Liu,Lingwen Kong,Lin Li,Zhang Jia,Jingpu Guo,Chenggang Zhuang,Lili Ding,Liping Chen,Fen Li,Kaicheng Zhang
DOI: https://doi.org/10.1360/982004-456
2005-01-01
Abstract:In the past few years, tremendous research activities have erupted since the discovery of the superconductivity in the simple binary compound, MgB2[1]. The interest is two-fold, one is dedicated to understanding the basic properties, and the other, to seeking for a mass production process of high quality wires, tapes, etc., toward largescaled applications. Application-wise, MgB2 is promising to substitute the Nb-based conventional superconductors due to its high transition temperature at 39 K. The operating temperature can be easily set at around 20 to 30 K,much higher than the liquid helium temperature. Hence,the required cryogenic environment can be conveniently obtained using a crycooler without the cumbersome facilities necessary to handle the cryogenic liquid. The benefits are obvious, immediate and immense. For example, an MgB2 superconducting magnet, without resorting to liquid helium, could reduce the size of a clinical MRI-CT system.The corresponding medical service would, therefore, become much more mobile and convenient, leading to a much easier and wider access in daily life. The impact would be apparent and far-reaching, and the significance cannot be overemphasized.