Preparation and Characterization of Polyurethane-Acrylate Hybrid Emulsion
Guo-wen Hu,Hui-fang Shen,Qing-feng Yang,Huan-qin Chen
DOI: https://doi.org/10.3321/j.issn:1000-565X.2007.06.014
2007-01-01
Abstract:Aqueous polyurethane (PU) prepolymers were synthesized by emulsion polymerization in situ, with toluene diisocyanate (TD1-80), polyether binary alcohol (N210), dimethylol propionic acid (DMPA), hydroxyl ethyl methacrylate (HEMA), adipic dihydrazide (ADH) and diacetone acrylamide (DAAM) as the materials. Three kinds of aqueous polyurethane-acrylate (PUA) hybrid emulsions marked as PUA-1 (free cross-linking), PUA-2 (synthesized cross-linking) and PUA-3 (cross-linking at ambient temperature) were synthesized after the free radical polymerization by adding initiator, which were then used to prepare three kinds of varnishes. The effects of the dosages of DMPA, HEMA, ADH and DAAM on the properties of emulsions and films were finally investigated. It is found that, when the mass fraction of -COOH in DMPA and the mass fractions of HEMA, ADH and DAAM in PU are respectively 2.5%, 1.44%, 3.5% and 2.0%-3.0%, the emulsions and films are all of good properties. Moreover, the results obtained by particle size analyzer and TEM show that (1) the average particle sizes of PUA-1, PUA-2 and PUA-3 are respectively 40-50 nm, 90-100 nm and 30-40 nm; (2) PUA-1 particles are regular sphericities in shape, while PUA-2 particles are irregular sphericities with interpenetrating polymer network between the core and the shell; (3) as compared with PUA-1, PUA-2 is of larger particle size and wider particle size distribution; (4) PUA-3 is of very irregular particle shape, uniform particle size distribution and disorganized interpenetrating network between the shell and the core. Furthermore, in the three kinds of vanishes, the one prepared from PUA-3 is of the best water resistance, dry-heat resistance and stain resistance but is of the longest drying time for the film.