Preparation and Properties of Magnetic Ag+/organic Zeolite 5A Composite Antibacterial Agent
WANG Qiong,FENG Qi-ming,LU Hao,WANG Wei-qing,HUANG Yang,WANG De-zhi,ZHANG Zhao
DOI: https://doi.org/10.3969/j.issn.1001-9731.2013.15.026
2013-01-01
Abstract:CoFe2O4 magnetic fluid and zeolite 5A which were prepared respectively by reflux method and hydrothermal synthesis,which were combined to produce a magnetic zeolite 5A with the different weight ratio of CoFe2O4,and then magnetic zeolite 5A were used to produce the magnetic silver type zeolite 5A by the ion exchange method.At last,the magnetic silver type zeolite 5A combined with the organic antibacterial agent was to produce magnetic Ag+/organic zeolite 5A composite antibacterial agent,which was characterized by the morphology,the size,the magnetic properties,the antibacterial properties,the magnetic separation recovery performance after dealing with the wastewater contained bacteria in the test.The results show that the granularity of CoFe2O4 was 12.7nm.CoFe2O4 has stable property and super paramagnetism.The zeolite 5A have cube crystal completely.The nanometer CoFe2O4 attached on the surface of zeolite 5A,magnetic zeolite 5A have super paramagnetism.The staturation magnetization(Ms),remanence magnetization(Mr) and coercive force(Hci) of magnetic zeolite 5A with CoFe2O4 contents of 25% were 17.842,4.8257A·m2/kg),0.427T,respectively.Antibacterial ratio of composite antibacterial agent to staphylococcus aureus and escherichia coli were 99.02% and 99.17% when the adsoption content of Ag+ reaches 271.71mg/g and the addition of organic antibacterial agent reaches 3.5%,respectively;the antibacterial agent can be recoveried from suspension with magnetic separation technology after the magnetic zeolite 5A was used to deal with wastewater contained bacteria.As the content of CoFe2O4 was 25%,the magnetic separation recovery rates of magnetic zeolite 5A composite antibacterial agent is 96.14%.