Preparation of Silver-Loaded Wollastonite Coatings and Study on Antibacterial Activity

冯宇,董宇启,曹聪,李宝娥,张继东

2008-01-01

Abstract:Objective To prepare the silver-loaded wollastonite coatings in order to obtain the bioactive implant material with antibacterial function.MethodsPlasma sprayed wollastonite coatings were immersed in 1%,5% and 9% AgNO3 solution for 24 h to load silver.They were evaluated by scanning electron microscopy,energy dispersive spectrometry,thin film X-ray diffraction and inductively coupled plasma-optical emission spectrometry to optimize the preparation process.The wollastonite coatings were prepared,the release rate of silver was measured and the antibacterial activity was examined.ResultsThe amount of silver loaded to wollastonite coatings increased with AgNO3 concentration.The processing technique of silver loading with 5% AgNO3 solution was selected for subsequent research.A sustained release of silver was detected in deionized water,lasting for 50 days.The bacteria inhibition zone lasted for 40 days,and the maximal diameter of bacteria inhibition zone reached(6.00±0.25)mm,significantly different from that without silver loading[(0.23±0.34)mm](P0.01).ConclusionWollastonite has chemical reaction to AgNO3 and produces silver silicate.The amount of silver loaded to wollastonite coatings increases with AgNO3 concentration.The silver-loaded wollastonite coatings prepared by the processing technique of silver loading with 5% AgNO3 solution have a favourable antibacterial activity.