Abstract:Gold catalysts supported on titania (Au-TiO(2)) and alumina (Au-Al(2)O(3)) were prepared by deposition-precipitation with urea and then activated before characterisation and reaction in CO oxidation, either by calcination in air at 500 °C or reduction under H(2) at 300 °C. Gold nanoparticles with average size in the range 2-4 nm were obtained, with calcination leading to larger gold nanoparticles than reduction. For Au-TiO(2), high activity was observed in CO oxidation at room temperature, independent of the activation treatment. This high activity could not be correlated to the presence of sub-nanometer gold clusters as reported in the literature, since they could not be detected by atomic-resolution high-angle annular dark-field scanning-transmission electron microscopy (HAADF-STEM). In the case of Au-Al(2)O(3), the performance in CO oxidation was found to strongly depend on the water content in the reaction gas feed and on the activation conditions, with calcination resulting in a poorly active catalyst whereas reduction gave activity of the same order as Au-TiO(2). A comparative study of Au-TiO(2) and Au-Al(2)O(3) by electron microscopy did not reveal distinct differences in the shapes of the Au nanoparticles, which are mostly flattened through interaction with the substrate in both samples, with side profile shapes varying from rounded hemispherical to well faceted truncated cubo-octahedra. More faceting is found for the samples calcined at 500 °C than reduced at 300 °C. Various possible parameters affecting the catalytic properties of gold in CO oxidation are discussed in the context of the relevant literature.

Influence of Preparation Methods on the Performance of Metal Phosphate-Supported Gold Catalysts in CO Oxidation

Study of Cyclohexane Oxidation over Au/Al_2O_3 Catalyst

Study of cyclohexane oxidation over Au/Al2O3 catalyst

Metal Phosphates As a New Class of Supports for Gold Nanocatalysts

Preparation of Highly Active Silica-Supported Au Catalysts for Co Oxidation by A Solution-Based Technique

Heterostructured Catalysts Prepared by Dispersing Au@Fe2O3 Core–shell Structures on Supports and Their Performance in CO Oxidation

Gold/Mg-Al mixed oxides catalysts for oxidative esterification of methacrolein: Effects of support size and composition on gold loading

Gold Nanoparticles on Electroless-Deposition-derived MnOx/C: Synthesis, Characterization, and Catalytic CO Oxidation

Au/PO43−/TiO2 and PO43−/Au/TiO2 Catalysts for CO Oxidation: Effect of Synthesis Details on Catalytic Performance

Au/MxOy/TiO2 Catalysts for CO Oxidation: Promotional Effect of Main-Group, Transition, and Rare-Earth Metal Oxide Additives

Effect of Pretreatment Atmosphere on CO Oxidation over Α-Mn2o3 Supported Gold Catalysts

Cerium Phosphate-Supported Au Catalysts for CO Oxidation

HRTEM and STEM-HAADF characterisation of Au-TiO2 and Au-Al2O3 catalysts for a better understanding of the parameters influencing their properties in CO oxidation

Activation of Dodecanethiol-Capped Gold Catalysts for Co Oxidation by Treatment with Kmno4 or K2mno4

Effect of Gold Electronic State on the Catalytic Performance of Nano Gold Catalysts in n-Octanol Oxidation

Gold nanoparticles supported on manganese oxides for low-temperature CO oxidation

Influence of hematite morphology on the CO oxidation performance of Au/α-Fe2O3

Research on unsupported nanoporous gold catalyst for CO oxidation

Catalytic behavior of gold nanoparticles supported on a TiO2-Al2O3 mixed oxide for CO oxidation at low temperature

A Rapid and Efficient Method to Deposit Gold Particles onto Catalyst Supports and Its Application for CO Oxidation at Low Temperatures

Oxidation of CO on gold supported catalysts prepared by laser vaporization: direct evidence of support contribution