Abstract:Chemical complex borohydride is a promising hydrogen storage material due to its large gravimetric and volumetric hydrogen capacities. However, the high dehydrogenation temperature and sluggish kinetics still place strong restrictions on its practical application in the hydrogen storage field. In this work, a synergetic approach of partial cation substitution and catalysis is developed to enhance the hydrogen storage properties of LiBH4. The Li/Mg based dual-cation borohydride (LiMg2(BH4)5, LMBH) was successfully synthesized by wet chemical ball milling of LiBH4 and MgCl2. The optimal (LMBH (4.5:1) sample, LiBH4 and MgCl2 in molar ratios of 4.5:1, possesses a maximum hydrogen desorption capacity (11.27 wt%) and the outstanding initial decomposition temperature (∼250 °C). Importantly, the LMBH (4.5:1) doped with TiF3 shows a remarkable onset dehydrogenation temperature as low as 97.2 °C, which is about 190 °C lower than that of pristine LiBH4. The LMBH (4.5:1) doped with TiF3 system releases 7.98 wt% H2 within 170 min below 350 °C. And the dehydrogenation product of doped composite can reversibly absorb ∼4.72 wt% H2 at a relatively moderate temperature of 280 °C, which is substantially lower than the reversible hydrogen absorption temperature of previous modified borohydride systems. Based on the structural characteristic analyses, the TiF3 reacts with LMBH (4.5:1) to in-situ form actual catalytic components of TiB2 and TiH2 as the actual catalysts for LMBH (4.5:1), resulting in the improved hydrogen re/dehydrogenation properties. The synergetic modification of Li/Mg dual-cation substitution and TiB2/TiH2 catalysis may lead to the development of light-metal borohydrides with outstanding hydrogen storage properties.

Low-Temperature Dehydrogenation of Libh4 Through Destabilization with Tio2

Dehydrogenation of LiBH<sub>4</sub>Destabilized with Various Oxides

Significantly Improved Dehydrogenation of Libh4 Destabilized by Tif3

Low-Temperature Hydrogen Desorption from Libh4-Tif4 Composite

In Situ Formation of TiB2 and TiH2 Catalyzed Li/Mg Based Dual-Cation Borohydride with a Low Onset Dehydrogenation Temperature below 100 °C

Hydrogen desorption from LiBH4 destabilized by chlorides of transition metal Fe, Co, and Ni

Destabilized dehydrogenation reaction of LiBH4 by AlF 3

Significant Destabilization Effects of Metal Borides on LiBH4

Destabilization of LiBH4dehydrogenation Through H+–H−interactions by Cooperating with Alkali Metal Hydroxides

Dehydrogenation in Lithium Borohydride/Conventional Metal Hydride Composite Based on A Mutual Catalysis

LiAlH4 As a “microlighter” on the Fluorographite Surface Triggering the Dehydrogenation of Mg(BH4)2: Toward More Than 7 Wt % Hydrogen Release below 70 °C

Excellent Low-Temperature Dehydrogenation Performance and Reversibility of 0.55Libh4-0.45Mg(bh4)2 Composite Catalyzed by Few-Layer Ti2C

Hydrogen Desorption Kinetics of the Destabilized LiBH 4 AlH 3 Composites

Metals (ni, Fe)-Incorporated Titanate Nanotubes Induced Destabilization of LiBH(4)

Hydrogen Storage Properties of LiBH4–Li3AlH6 Composites

Dehydrogenation/rehydrogenation mechanism in aluminum destabilized lithium borohydride

Enhanced Hydrogen Storage Properties of LiBH4 Modified by NbF5

Promotion Mechanisms of LiBH4 Dehydrogenation Dominated by Charge Redistribution

Destabilization and Regeneration of LiBH4 Using N-containing Hydrocarbon Based Polymers for Hydrogen Storage

Destabilization of LiBH4 by (ce, La)(Cl, F)3 for Hydrogen Storage

Destabilized LiBH4-NaAlH4 mixtures doped with titanium based catalysts