Elastic Constant Anomalies in Sinter-Forged High-Tc Superconductor YBa2Cu3O7 − Δ

Z ZHAO,S ADENWALLA,A MOREAU,JB KETTERSON,Q ROBINSON,DL JOHNSON,SJ HWU,KR POEPPELMEIER,MF XU,Y HONG,M LEVY,BK SARMA

DOI: https://doi.org/10.1016/0022-5088(89)90522-5

1989-01-01

Journal of the Less Common Metals

Abstract:The ultrasound velocity in the sinter-forged YBa2Cu3O7 − δ superconductor was measured and the results showed evident anomalies as well as anisotropies. Both longitudinal and shear wave velocity along the c axis (the forging axis) showed a distinct thermal hysteresis from 65 K to 260 K. The velocity change ΔVV from room temperature to 4 K was 1.5%. The sound velocity along the “basal plane” reached a maximum around 160 K. No distinct thermal hysteresis was observed. ΔVV from room temperature to 4 K was 1%. All of these velocities were measured while sweeping the magnetic field up to 9 T at fixed temperatures of 4 K and 86 K respectively. No velocity change was observed. The shear wave velocity behaved similarly at 9 T during the thermal cycling between room temperature and 4 K.