Abstract:In this work the preparation mechanism, properties and temperature-triggered aggregation of poly(D, L-lactide- co-glycolide) (PLGA) dispersions are investigated. The dispersions were prepared by interfacial deposition in aqueous solution containing Pluronic L62 (EO(6)PO(30)EO(6)) or F127NF (EO(101)PO(56)EO(101)), where EO and PO are ethylene oxide and propylene oxide, respectively. PLGA dispersions were also prepared in the absence of added Pluronic for comparison. The PLGA particles were characterized using SEM, photon correlation spectroscopy and electrophoretic mobility measurements. It was found that the hydrodynamic diameter (d) increased with PLGA concentration used in the organic solvent phase ( C PLGA(o) ). The value for d was proportional to C(PLGA)(o) (1/3). The value for d increased upon addition of 0.04 M NaNO(3) which demonstrated the importance of electrostatic interactions during particle formation. Electrophoretic mobility measurements were conducted as a function of pH and the data used to estimate the Pluronic layer thicknesses on the PLGA particles. The layer thickness was greatest for the PLGA particles prepared in the presence of Pluronic F127NF. PLGA dispersions containing Pluronic L62 exhibited temperature-triggered aggregation in the presence of 0.15 M NaNO(3). It was found that the critical temperature for dispersion aggregation (T(crit)) was comparable to the cloud point temperature ( T(cp)) for the parent Pluronic L62 solution. Conditions were established for achieving temperature-triggered aggregation at body temperature for PLGA particle/Pluronic L62 dispersions under physiological ionic strength and pH conditions. The PLGA/Pluronic L62 mixtures studied may have potential for use as injectable biodegradable implants for controlled release applications.

Study of Poly(l-Lactide) Microparticles Based on Supercritical CO2

Preparation of Poly L-Lactide Microspheres by Supercritical CO2 Antisolvent Processing

Preparation of PLLA Microparticles by Supercritical CO2 Anti-solvent Technology

Study of Lysozyme‐polymer Composite Microparticles in Supercritical CO2

Preparation of water soluble drugs-loaded microparticles using modified solution enhanced dispersion by supercritical CO 2

Preparation of PLLA/PLGA Microparticles Using Solution Enhanced Dispersion by Supercritical Fluids (SEDS).

Study of Lysozyme-Loaded Poly-L-Lactide (plla) Porous Microparticles in A Compressed Co2 Antisolvent Process

Study of Magnetic Polymer Microparticles Based on Supercritical Co2

Preparation of Poly (L-Lactic Acid) Microsphere

Preparation of 5-fluorouracil-poly(L-lactide) microparticles by supercritical fluids technique

Poly(d,l-lactide-co-glycolide) Dispersions Containing Pluronics: from Particle Preparation to Temperature-Triggered Aggregation

Synthesis of Cross-Linked Poly ( N -Isopropylacrylamide) Microparticles in Supercritical Carbon Dioxide

Co-precipitation of 10-hydroxycamptothecin and poly (l-lactic acid) by supercritical CO2 anti-solvent process using dichloromethane/ethanol co-solvent

Preparation of PLA-PEG nanoparticles by the solution enhanced dispersion with enhanced mass transfer using ultrasound in supercritical CO 2

Preparation of Morphology-Controllable Microcellular Polylactide Acid by Supercritical Carbon Dioxide

A Continuous RESS Process to Prepare PLA–PEG–PLA Microparticles

Effect of Process Parameters on Co-Precipitation of Paclitaxel and Poly(L-Lactic Acid) by Supercritical Antisolvent Process

Formation of l-poly(lactic acid) microspheres by rapid expansion of CO2 saturated polymer suspensions

The Preparation of BSA-PLLA Microparticles in a Batch Supercritical Anti-Solvent Process

Characterization and biological evaluation of paclitaxel-loaded poly(L-lactic acid) microparticles prepared by supercritical CO2.

Development of Fe3O4-poly(L-lactide) magnetic microparticles in supercritical CO2.