Abstract:Polypropylene color masterbatches containing modified layered double hydroxides, LDHs, were created. The simple, industry-acceptable method of LDH surface modification with quinacridone and phthalocyanine pigments using the pulverization method in ball mills was applied. It was reported that the modification parameters such as time and rotational speed affected the tendency to create the aggregates for modified fillers. TGA analysis of the modified LDH showed that modification with phthalocyanine pigment shifted the temperature at which 5%, T5%, and 10% of mass loss, T10%, occurred compared with that for unmodified LDH. The viscoelastic properties of prepared masterbatches were investigated. The incorporation of the modified fillers instead of neat pigments led to an increase in the loss shear modulus, G″, indicating a stronger influence on the dissipation of energy by the melted masterbatch. The similar values of tan, δ, were determined for melted masterbatches containing phthalocyanine pigment and green modified LDH filler. The incorporation of both LDHs modified by phthalocyanine and quinacridone pigment fillers slightly increased the zero-shear viscosity, η0, compared with that of the masterbatches based on the neat pigments. The Cole-Cole plots and the analysis of the Maxwell and continuous relaxation models showed that modified colored LDH fillers facilitated the relaxation of the melted masterbatch, and shorter relaxation times were observed. The phthalocyanine-modified LDH filler improved the thermal stability of the masterbatches. Additionally, the impact of pigments and modified, colored LDH on the crystallization of polypropylene was investigated.

Effect of Nano-BaSO_4 on Color Properties of High Concentration Polyolefine Masterbatch

EFFECT OF NANO-CaCO3 ON COLOR PROPERTIES OF HIGH CONCENTRATION POLYOLEFINE MASTERBATCH

Effect of Low‐concentration Alkali Solution Pretreatment on the Properties of Bamboo Particles Reinforced Poly(lactic Acid) Composites

Modification Of Mechanical And Color Properties Of Polypropylene With Colored Nano-Sio2 Prepared From Diatomite

Modification of mechanical and color properties of polypropylene with colored nano‐SiO<sub>2</sub> prepared from diatomite

Effect of Oleic Acid-modified Nano-CaCO3 on the Crystallization Behavior and Mechanical Properties of Polypropylene

Crystallization and Mechanical Properties of Polypropylene Filled with Sio2 Nanoparticles

Filling And Coloring Effect Of Pearl Shell Powder And Dye-Loaded Pearl Shell Powder On Polypropylene

Effect of Barium Sulfate Nanoparticles on Mechanical Properties and Crystallization Behaviour of Hdpe

Colorating and Mechanical Performance of Low-Density Polyethylene (Ldpe)/dye-Loaded Shell Powder (DPSP) Composites

Application of Nanotechnology in Water-based Colorant

Bio‐based polyethylene masterbatch preparation and investigation of the effect of process conditions on pigment dispersion

Sustainability in the Development of Natural Pigment-Based Colour Masterbatches and Their Application in Biopolymers

Preparation, Characterization And Filling Effect Study Of Dye-Loaded Shell Powder On The Properties Of Ldpe Composite

Sustainable preparation of nano monodispered ATP based color master batch and its application in PA6

Influence of Nano Particles on Adhesion Strength of Polyethylene with Steel Substrates

Effect of nano-carbon addition on color performance of polystyrene superstructure film

Polypropylene Color Masterbatches Containing Layered Double Hydroxide Modified with Quinacridone and Phthalocyanine Pigments-Rheological, Thermal and Application Properties

Effect of nano-sized Al2O3-particle addition on PVDF ultrafiltration membrane performance

Water-Assisted Melt Compounding Preparation and Property of Nylon6/Nano-MMT Masterbatch

Effect of Nano-MgO Particles Doping on Breakdown Characteristics of Polypropylene