Abstract:NH4Cl corrosion failure often occurs in the overhead systems of hydrotreaters, and this failure is always accompanied by the appearance of H2S. A combination of electrochemical and surface spectroscopic (SEM/EDS, AFM, XRD) techniques was used to investigate the effect of different factors, including the surface roughness, temperature, dissolved oxygen, pH and H2S concentration, on the corrosion behavior of carbon steel in an NH4Cl environment with the presence of H2S. The effect of H2S concentrations (at the ppm level) on the corrosion behavior of carbon steel was systematically revealed. The experimental results clearly indicated that the corrosion rate reached a minimum value at 10 ppm H2S. The steel surface was covered by a uniform corrosion product film in a 10 ppm H2S environment, and the corrosion product film was tight and protective. The ammonia from NH4Cl helped maintaining the protectiveness of the corrosion films in this environment. Dissolved oxygen mainly accelerated the cathodic reaction. The cathodic limiting current density increased with increasing temperature, and the anodic branch polarization curves were similar at different temperatures. The anodic current density decreased as the pH decreased, and the cathodic current density increased as the pH decreased. The absolute surface roughness (R (a)) of carbon steel increased from 132.856 nm at 72 h to 153.973 nm at 144 h, and the rougher surface resulted in a higher corrosion rate. The critical innovation in this research was that multiple influential factors were revealed in the NH4Cl environment with the presence of H2S.

Corrosion of low carbon steel in atmospheric environments of different chloride content

Effects of chloride ions on corrosion of ductile iron and carbon steel in soil environments

Corrosion Characteristics of Low-Carbon Steel in Hot and Humid Industrial-Marine Atmosphere

Corrosion Behavior of Q235 Steel in Atmospheres Containing SO2 and NaCl

The Atmospheric Corrosion Kinetics of Low Carbon Steel in a Tropical Marine Environment

Effect of chloride ion content on the corrosion resistance of weathering steel

Corrosion behavior of weathering steel in marine atmosphere

Insights into the Corrosion Mechanism and Electrochemical Properties of the Rust Layer Evolution for Weathering Steel with Various Cl− Deposition in the Simulated Atmosphere

Corrosion of steel materials in four environmental conditions

Corrosion Behavior of Galvanized Steel in Simulated Coastal-Industrial Atmosphere

Influence of Cl- and SO2 on Carbon Steel Q235, Pipeline Steel L415 and Pressure Vessel Steel 16MnNi Corrosion Behavior in Industrial and Marine Atmosphere Environment

Atmospheric chloride-induced corrosion of steel-reinforced concrete beam exposed to real marine-environment for 7 years

Synergistic Effect of Different NaCl Concentrations on the Initial Corrosion of Q235 Steel under a Simulated SO2 Environment

Investigation on the initial atmospheric corrosion of mild steel in a simulated environment of industrial coastland by thin electrical resistance and electrochemical sensors

Unraveling the effect of chloride ion on the corrosion product film of Cr-Ni- containing steel in tropical marine atmospheric environment

Corrosion Behaviour of Low-Carbon Bainitic Steel under a Constant Elastic Load

Effect of Temperature on Corrosion Behavior of Low-Alloy Steel Exposed to a Simulated Marine Atmospheric Environment

A Study on the Corrosion Behavior of Carbon Steel Exposed to a H2S-Containing NH4Cl Medium

Influence of Carbon Content and Microstructure on Corrosion Behaviour of Low Alloy Steels in a Cl− Containing Environment

A Study on the Interaction Between Chloride Ions and CO2 Towards Carbon Steel Corrosion

CORROSION BEHAVIOR OF RUSTED MILD STEEL UNDER MEANS OF WET/DRY ALTERNATE CONDITIONS