Abstract:The microstructure and hydrogen storage properties of Ti10+xV80-xFe6Zr4 (x = 0, 5, 10, 15) alloys have been studied. XRD and SEM analyses show that all alloys consist of a BCC main phase and a small fraction of C14 Laves secondary phase, in which the latter precipitates along the grain boundary of the former becoming network structure. With increasing Ti content in the alloy, the lattice parameter and cell volume of the BCC main phase of the alloy increase. The chemical composition of each phase is analysed by EDS, from which the lattice parameters of BCC phase have a good linear relationship with their average atomic radii. All bulk alloys have good activation behaviors and hydriding kinetics. With the increase of Ti content, the incubation time for activation decreases first and then increases under an initial hydrogen pressure of 4 MPa at 298 K. The incubation time of Ti15V75Fe6Zr4 alloy is only 12 s. It is one of the shortest incubation time in V-based solid solution alloys as far as we know, which may be related to the existence of C14 Laves phase. All the alloys have relatively high hydrogen absorption capacities of above 3 wt%, which increase first and then decrease as the Ti content increases, achieving the maximum capacity of 3.61 wt% at x = 10 at 298 K. With increasing x, the equilibrium plateau pressure of dehydrogenation of the samples at 353 K decreases owing to the expansion of unit cell of main phase, which is far below 0.1 MPa for x = 10 and 15. The maximum desorption capacity of 1.94 wt% (desorbed to 0.001 MPa) is obtained at x = 5, compared to that of 1.6 wt% (desorbed to 0.1 MPa) achieved at x = 0.

Hydrogen Desorption Properties and Electrode Performances of Ti–Zr–Ni–V–Mn Alloy

Development of Ti–Zr–Mn–Cr-(V–Fe) Based Alloys for Hydrogen Feeding System in Hydrogen Metallurgy Application

Phase Structures and Electrochemical Properties of V2.1TiNi0.4Zrx (x=0−0.06) Hydrogen Storage Electrode Alloys

Microstructure and Electrochemical Properties of V_(2.1)TiNi_(0.4)Zr_(0.06)Cu_(0.03)M_(0.10)(M=Cr, Co, Fe, Nb, Ta) Hydrogen Storage Alloys

Microstructure and Electrochemical Properties of V2.1TiNi0.4Zr0.06Cux (X=0-0.12) Hydrogen Storage Alloys

Hydrogen Storage Properties of Ti-Cr-Mn-M (M=V, Fe, Ni, Cu) Alloys

Hydrogen absorption-desorption characteristics of Ti0.35Zr0.65NixV2−x−yMny alloys with C14 Laves phase for nickel/metal hydride batteries

Microstructures and Hydrogen Storage Properties of Ti10V83-xFe6ZrMnx Alloys

Preparation and Evaluation of Electrode Materials for Nickel/metal Hydride Batteries

Structural and Electrochemical Properties of Hydrogen Storage Alloys Ti0.8Zr0.2V2.7Mn0.5Cr0.8Nix (x = 1.50–2.25)

Microstructure and hydrogen storage properties of Ti10+xV80-xFe6Zr4 (x=0~15) alloys

Investigation of Microstructure and Electrochemical Properties of Ti0.8Zr0.2V2.7Mn0.5+xCr0.8Ni1.5−x Hydrogen Storage Alloys

V 2.1 TiNi 0.4 Zr 0.06 Cu 0.03 M 0.10 (M=Cr, Co, Fe, Nb, Ta)储氢合金的微结构及电化学性能

The microstructure and electrochemical properties of Ti0.3Zr0.225V0.25Mn0.3-xNi0.45+x (x=0 similar to 0.25) Ti-based hydrogen storage alloys

Hydrogen storage capabilities of the alloys Fe 0.85Mn 0.15Ti 0.9M 0.1 (M=Zr, V, Ca)

The phase structures and electrochemical properties of TiV2.1Nix(x=0.2 similar to 0.6) hydrogen storage alloys

Hydrogen storage properties of TiMn2-based alloys

Phase Structures And Hydrogen Storage Capabilities Of The Alloys (Ml)(X) (Ni3.8co0.75mn0.4ti0.05)

The Effects of Partial Substitution of Mn by Cr on the Phase Structure, Microstructure and Electrochemical Properties of Ti-Zr-V-Mn-Ni Hydrogen Storage Alloys

Study on the microstructure and electrochemical properties of Zr-Ti-Mn-Ni hydride alloy

Electrochemical studies on the Ti–Zr–V–Mn–Cr–Ni hydrogen storage electrode alloys