Abstract:Achieving the effective joining between Al alloy and stainless steel with a large cross-section was meaningful in the significant industry field. For this, the Al/steel dissimilar bimetal materials were manufactured by a novelty hybrid technology, named thermo-compensated resistance brazing welding. The effect of the single Zn foil and the depos-ited Zn coatings with cold spray technology on the bonding interface, interfacial micro-structure, and mechanical properties of the final Al/steel resultant joints were systematically investigated by the relevant analysis method. The results revealed that the obvious reaction layer with main components of Al(s.s) was formed at the Al/steel joints with the single Zn foil as the interlayer. Meanwhile, the introduction of the Zn interlayer improved the temperature field of the joint, which enhanced the lap-shear load of the weld. Besides, the Zn coating was deposited at the top surface of the 304ss substrate as the interlayer to increase joint performance further. The advantage of the pre-deposition formed a better metallurgical bond between the coating and 304ss. The subsequent lap-shear load of the weld was improved with the increase of the Zn coating thickness. The maximum lap-shear load of the final joints reached 2087.6N with a Zn coating thickness of 500 mm and the interfacial structure of the joint was changed: Al alloy, reaction layer I, Al(s.s) thorn Al2O3, and 304ss from top to bottom. The main composition was Al(s.s) at the reaction layer I between Al alloy and coating.& COPY; 2023 Published by Elsevier B.V. This is an open access article under the CC BY-NC-ND license (http://creativecommons.org/licenses/by-nc-nd/4.0/).

Brazing Process for Outer Shell Sandwich Structure of Vehicle-mounted Storage Tank and Its Mechanical Properties

STRESS TEST ANALYSIS OF 15×10~4 m~3 FLOATING ROOF TANK MADE OF HOME-MADE STEEL PLATE

Microstructure and mechanical properties of brazing joint of silver-based composite filler metal

Effect of Brazing Parameters on Microstructure and Mechanical Properties of Ti5Si3/Ti3Al Composite Joints Brazed with Ti–Zr–Cu–Ni Filler Alloy

Study of Microstructure and Fatigue in Aluminum/Steel Butt Joints Made by CMT Fusion-Brazing Technology

TIG welding-brazing joints of aluminum-stainless steel with different thickness of base metals

Brazing Oxide Dispersion-Strengthened Fe-Based Steels with a Cu-Based Filler Metal

Study on laminar structure and process on high strength brazed aluminum alloy for heat exchangers

Effect of Brazing Temperature on Tensile Strength and Microstructure for a Stainless Steel Plate-Fin Structure

Study on the interface microstructure and mechanical properties of 5005 aluminum alloy and stainless steel brazed joint

Microstructure and Strength of Brazed Joints of Ti3al-Base Alloy with Different Filler Metals

Microstructure and Mechanical Performance of Gta Weld Brazed Joints of Copper Thick Plates

Effect of Bevel Angle on Microstructure and Mechanical Property of Al/steel Butt Joint Using Laser Welding-Brazing Method

Effect of Brazing Fillet on the Microstructure and Mechanical Properties of Vacuum Brazing Stainless Steel Joints

Impact of various heat treatment processes and welding speeds on the mechanical properties and microstructures of soft/hard composite joints

Microstructures and Mechanical Properties of Stainless Steel Clad Plate Joint with Diverse Filler Metals

Microstructure and Mechanical Properties of TIG Brazing of Stainless Steel

Numerical investigating the effect of braze processing parameters on residual stresses in an X-type lattice truss sandwich structure

Interfacial Microstructure and Mechanical Properties of Al/steel Joints Fabricated Via Thermo-Compensated Resistance Brazing Welding with Cold Spray Zn Interlayer

Interfacial Microstructure and Mechanical Properties of Dissimilar Aluminum/steel Joint Fabricated Via Refilled Friction Stir Spot Welding

Effect of Brazing Temperature on Tensile Strength and Microstructure for 304 Stainless Steel Plate-Fin Structure