Abstract:The catalytic performances over propylene epoxidation with H 2 and O 2 (HOPO process) are significantly affected by the properties (e.g., surface properties, Ti coordination, and morphology) of titanosilicate zeolite. Introducing urea into zeolite synthesis is a simple and convenient method to modify these properties of titanosilicate zeolite. Uncalcined pore-blocked titanium silicalite-1 (TS-1, i.e., TS-1-B) with the lower urea dosage possesses more defective structure and unsaturated coordinated Ti sites verified by 29 Si nuclear magnetic resonance (NMR) and X-ray photoelectron spectroscopy (XPS) analysis, which results in a high initial activity and hydrogen efficiency; while the high surface acidity generated by these Ti species leads to a continuous decrease in the activity and the propylene oxide (PO) selectivity during the reaction. As the amount of urea gradually increases, the TS-1-B samples present the reduced surface defects and defective and unsaturated Ti species. Specially, TS-1-B-0.30U presents the weaker PO adsorption on PO-diffusion reflectance infrared Fourier transform spectra (DRIFTS), and thus results in the high stable PO formation rate and selectivity over its Au catalyst. Furthermore, a flat-plate-like shape with a shorter thickness of 100 nm along the b-axis direction is observed on the urea-modified TS-1. Compared with the conventional ellipsoidal TS-1 with crystal sizes of 200 and 500 nm, the flat-plate-like TS-1-0.30U displays the less surface defects, unsaturated Ti species, and the weaker Lewis acid, which is favorable for the desorption and intracrystalline diffusion of PO, thus reduces the occurrence of side reactions for the improved selectivity and stability. This work may provide a reference for developing titanium-containing materials with high activity and stability over HOPO reaction.

Effect of Alkaline Additive on Propylene Epoxidation Catalyzed by TS-1 in Supercritical CO2

Effect of Alkaline Additive on Propylene Epoxidation Catalyzed by Large Grain Size TS-1 in Supercritical CO2

Epoxidation of propylene to propylene oxide catalyzed by large-grain TS-1 in supercritical CO2

Epoxidation of propylene to propylene oxide catalyzed by μ-oxo-bismetalloporphyrins

Factors Affecting Propylene Epoxidation Catalyzed by Reaction-Controlled Phase-Transfer Catalyst

Promotional Effect of Y2O3 on the Performance of Ag/α-Al2O3 Catalyst for Epoxidation of Propylene with Molecular Oxygen

Influence of Acid-Base Properties of ZnMgAl-mixed Oxides for the Synthesis of 1-Methoxy-2-propanol

Role of Chlorohydrocarbon in Increasing Selectivity of Propylene Oxide over Ag–Y2O3–K2O/α-Al2O3 Catalyst for Epoxidation of Propylene by Molecular Oxygen

Aliphatic Olefin Epoxidation with Hydrogen Peroxide Catalyzed by an Integrated Mn/TS-1/N System

Effect of Ag addition on performance of Au/TS-1-B catalyst in gas phase propylene epoxidation

Lewis Acid Property and Catalytic Performance of MoO3/SiO2 for Propylene Epoxidation by CHP: Effects of Precipitant Ph Value and Rare Earth Additive

Deactivation of catalyst TS-1 in propene epoxidation

Insight into the Effect of Mass Transfer Channels and Intrinsic Reactivity in Titanium Silicalite Catalyst for One-Step Epoxidation of Propylene

Effect of Additive in Feedstock on Performance of Ag-MoO3/ZrO2 Catalyst for Propylene Epoxidation by Molecular Oxygen

Direct epoxidation of propylene by molecular oxygen over Y2O3 and K2O-promoted Ag/α-Al2O3 catalyst

Study on Ag-Mo Catalyst for Direct Vapor-Phase Epoxidation of Propylene by Molecular Oxygen

Au/TS-1 catalyst for propylene epoxidation with H2 and O2: Effect of surface property and morphology of TS-1 zeolite

Towards highly stable and active Au / uncalcined TS-1 catalysts for direct propylene epoxidation with molecular H 2 and O 2 : Effect of Si / Ti molar ratio

Au/uncalcined TS-1 Catalysts for Direct Propene Epoxidation with H2 and O2: Effects of Si/Ti Molar Ratio and Au Loading

Direct Epoxidation of Propylene on Nacl-Modified Cu/Sio2 Catalysts Using Air As Oxidant

Advances in Manipulation of Catalyst Structure and Relationship of Structure Performance for Direct Propene Epoxidation with H-2 and O-2