Abstract:Numerous studies have demonstrated that under low-velocity, low-energy impact conditions, although the surface damage to fiber-reinforced composite laminates may be minimal, significant internal damage can occur. Consequently, a progressive damage finite element model was specifically developed for thermoplastic carbon fiber-reinforced composite laminates subjected to low-speed impact loads, with the objective of analyzing the damage behavior of laminates under impacts of varying energy levels. The model utilizes a three-dimensional Hashin criterion for predicting intralayer damage initiation, with cohesive elements based on bilinear traction-separation law for predicting interlaminar delamination initiation, and incorporates a damage constitutive model based on equivalent displacement to characterize fiber damage evolution, along with the B-K criterion for interlaminar damage evolution. The impact response of laminates at energy levels of 5 J, 10 J, 15 J, 20 J, and 25 J was analyzed through numerical simulation, drop-hammer experiments, and XCT non-destructive testing. The results indicated that the simulation outcomes closely correspond with the experimental findings, with both the predicted peak error and absorbed energy error maintained within a 5% margin, and the trends of the mechanical response curves aligning closely with the experimental data. The damage patterns predicted by the numerical simulations were consistent with the results obtained from XCT scans. The study additionally revealed that the impact damage of the laminates primarily stems from interlaminar delamination and intralayer tensile failure. Initial damage typically presents as internal delamination; hence, enhancing interlaminar bonding performance can significantly augment the overall load-bearing capacity of the laminate.

Low-Velocity Impact Characteristics of Carbon Fiber Composites Lattice Core Sandwich Structures

Damage Propagation Behavior of Composite Honeycomb Sandwich Panels Under Low-Velocity Impact

Experimental and numerical investigations on the dynamic response of woven carbon fiber reinforced thick composite laminates under low-velocity impact

Exploration of Several Influence Factors of Low-Velocity Impact Damage on Composite Laminates

Investigation of Damage to Thick Composite Laminates under Low-Velocity Impact and Frequency-Sweep Vibration Loading Conditions

Changes in Dynamic Mechanical Behavior of Carbon Fiber Reinforced Polymer Laminates under Multiple Low Energy Impacts

Impact Resistance of Thin Plain Woven Composite Laminates under High-velocity Small Mass Impact

Low-velocity Impact Damage Analysis in Composite Laminates

Experimental Investigation of Low-velocity Impact and Residual Compressive Strength of Composites

Low‐velocity multiple impact damage characteristics and numerical simulation of carbon fiber/epoxy composite laminates

Numerical Investigation on the Repeated Low-Velocity Impact Behavior of Composite Laminates

Experimental Investigation of the Double Impact Position Effect on the Mechanical Behavior of Low-Velocity Impact in CFRP Laminates

Low-velocity Impact Responses and Failure of Sandwich Structure with Carbon Fiber Composite Honeycomb Cores

Experimental and Simulation Study on Failure of Thermoplastic Carbon Fiber Composite Laminates under Low-Velocity Impact

Research on low‐velocity impact resistance of carbon fiber composite laminates

Damage and Failure of Laminated Carbon-Fiber-Reinforced Composite under Low-Velocity Impact

Experiments and Finite Element Simulations of Composite Laminates Following Low Velocity On-Edge Impact Damage

Low-velocity Impact Behavior of X-Frame Core Sandwich Structures – Experimental and Numerical Investigation

Experimental Study on High-velocity Impact Damage Behavior of Carbon Fiber Reinforced Composite Laminates

Experiment and finite element analysis of lattice reinforced composite sandwich panels subjected to low-velocity impact

Experimental Study on Low-Velocity Impact Performance of Carbon Fiber Reinforced Composite Laminates