Thermophysical properties and rapid solidification mechanism of liquid Zr 60 Ni 25 Al 15 alloy under electrostatic levitation condition
Jin Ying-Jie,Geng De-Lu,Lin Mao-Jie,Hu Liang,Wei Bing-Bo
DOI: https://doi.org/10.7498/aps.73.20232002
IF: 0.906
2024-01-01
Acta Physica Sinica
Abstract:In this study, the thermophysical properties and rapid solidification mechanism of highly undercooled liquid Zr 60 Ni 25 Al 15 alloy were investigated through the electrostatic levitation technique. The maximum undercooling of this alloy has attained 316 K (0.25 T L ). Both density and surface tension displayed a linear relationship with temperature, while viscosity demonstrated an exponential temperature dependence. When alloy undercooling was less than 259 K, two significant recalescence events were observed during solidification, corresponding to the formation of pseudobinary (Zr 6 Al 2 Ni + Zr 5 Ni 4 Al) eutectic and ternary (Zr 6 Al 2 Ni + Zr 5 Ni 4 Al + Zr 2 Ni) eutectic. The growth velocity of the binary eutectic phase gradually increased with undercooling and reached the maximum value at an undercooling of 259 K. In contrast, once undercooling surpassed 259 K, a single recalescence event occurred, leading to the independent nucleation of all three compound phases from alloy melt and the rapid growth of a ternary anomalous eutectic structure. Notably, the growth velocity of the ternary eutectic phase exhibited a gradual decline with the continued increase in undercooling. This diminishing trend of the growth velocity suggests, hypothetically, that further increasing the undercooling might entirely suppress crystal growth dynamically at a threshold of 385 K. With classical nucleation theory and the Kolmogorov-Johnson-Mehl-Avrami (KJMA) model, the onset of crystallization for the three phases was calculated, leading to construct a time-temperature-transformation (TTT) diagram. This diagram elucidates the competitive nucleation among the three phases in the undercooled melt. Both theoretical and experimental evidences revealed that Zr 6 Al 2 Ni phase primarily nucleated at lower undercooling levels, whereas the simultaneous nucleation of all three phases becomes feasible at higher undercooling.
physics, multidisciplinary