Abstract:A series of the double-doping samples La(2+4x)/3Sr(1−4x)/3Mn1–xCuxO3 (0⩽x⩽0.2)with the Mn3+/Mn4+ ratio fixed at 2:1 and the single-doping samples La2/3Sr1/3Mn1–xCuxO3 (0⩽x⩽0.2) have been investigated. For the double-doping samples, though the ratio Mn3+/Mn4+=2:1 has been generally recognized the optimum ratio, the Curie temperature TC and metallic–insulator transition temperature Tp1 are more rapidly decreased by Cu substitution than that corresponding to single-doping samples. And the resistivity ρ value for the double doping is larger about two or three orders of magnitude than that corresponding to single doping. At the same time, two resistivity peaks and two magnetoresistance (MR) peaks appear. We suggest that for the double-doping samples the A-site cation size 〈rA〉 and the A-site mismatch factor σ2 decreases with increasing doping level, which leads to the system microstructural distortion. This microstructural distortion makes the Mn3+–O–Mn4+ cut off more cluster-spin except for the clusters induced by Cu. These cluster interfaces contribute to ρ, which exceeds far the contribution of eg electron decreasing with doping increasing in the single doping. At the same time, such interface scattering also gives rise to the appearance of second peak for the double-doping samples. The experimental results shows that double doping could be also a potential way in tuning colossal MR (CMR), which can give a guide for the adequate selection of CMR materials.

Coexistence Of Pd Sigma Hybridization Conduction And Double-Exchange Conduction In Heavily Doped La1.85-2xsr0.15+2xcu1-Xmxo4

Coexistence of p d σ hybridization conduction and double-exchange conduction in heavily doped La1.85-2xSr0.15+2xCu1-x MnxO4

Coexistence of pd σ hybridization conduction and double-exchange conduction in heavily doped La 1.85 − 2 x Sr 0 . 1 5 + 2 x Cu 1 − x Mn x O 4

Two conduction mechanisms in the double doping La1.85–2xSr0.15+2xCu1–xMnxO4 system

Anomalous Transport Properties Of Heavily Doped Polycrystalline La0.825sr0.175mn1-Xcuxo3

Magnetic and Transport Properties in Double-Doping La(2+4x)/3Sr(1−4x)/3Mn1–xCuxO3 (0⩽x⩽0.20) Systems

Effect of Li doping and Li, La co-doping on the structure and physical properties of LaBa2Cu3Oy

Anomalous Transport Properties of Heavily Doped Polycrystallinela0.825sr0.175mn

Electric and Magnetic Behaviour in Double Doped La2/3+4x/3Sr1/3−4x/3Mn1−xMgxO3

Superconductivity and Magnetism in the Mixed-Valence Mn Doped La1.85−1.5xSr0.15+1.5xCu1−xMnxO4 System

Reentrance of Interface Superconductivity in a High-Tc Cuprate Heterostructure

Superconductivity, Magnetic Susceptibility and Electrical Resistivity of the Double-Doped La1.85−xSr0.15+xCu1−xCoxO4 (0 ≤ X ≤ 0.4)

Superconductivity Inla1.85−4∕3xsr0.15+4∕3x

Charge Transport in La2−xSrxCuO4 in the Low-Density Limit (0.03 < X < 0.10)

Charge transport in La2-xSrxCuO4 in the low-density limit (0.03 < x < 0.10)

Transport Mechanism In Polycrystalline La0.825sr0.175mn1-Xcuxo3

Percolative Conductivity and Superconductivity in La1.85−xSr0.15+xCu1−xMnxO4

Lattice structure and transport properties of the system La (1+x)/3Ba (2-x)/3Mn xCu 1-xO 3 (0.8≤x≤1)

Magnetic and transport properties of the Co-doped manganite La0.7Sr0.3Mn1-xCoxO3 (0 ≤x ≤ 0.5)

Effect of Cu doping at the Mn site on the transport and magnetic behaviors of La2/3Ca1/3MnO3

Superconductivity coexisting with ferromagnetism in mixed-valence Mn doped La1.85−(4/3)xSr0.15+(4/3)xCu1−xMnxO4