Preparation and Properties of Aliphatic Polyurethane/hydroxyapatite Composites by in Situ Polymerization

LIU Hao-huai,ZHANG Li,ZUO Yi,LI Ji-dong,ZOU Qin,LI Yu-bao

2010-01-01

Abstract:In order to avoid toxic degradation products of aromatic polyurethanes in vivo,aliphatic polyurethanes with good biocompatibility and bioactive hydroxyapatite were selected to fabricate porous PU/HA scaffolds for tissue engineering by in situ polymerization.The morphology and properties of the scaffolds were characterized by SEM,IR,and mechanical testing.The effects of the amount of blowing agent(water) and HA content on the pore structure and mechanical strength of scaffolds were investigated.The results indicate that when adding 1wt%-1.5wt% blowing agent into PU,the scaffolds possess interconnected porous structure with a pore size mainly ranging from 300 to 800μm,and 50-200μm micropores existed on the pores' walls,the porosity of the scaffolds is more than 80%.The compressive strength and modulus of the composite scaffolds show higher enhancement with increasing HA content.Considering comprehensively the reinforcing effect of the HA filler and the open porous structure for tissue engineering scaffold,in this system,the optimal addition of HA particles in polyurethane can be 40wt% and the optimal amount of blowing agent can be 1wt%.