Abstract:Cr-Cu-N coatings with copper content from 0 at% to 6.8 at% were deposited on silicon and M2 steel by ion beam assisted magnetron sputtering. The microstructure and composition of the coatings were characterized using SEM, GDOES, XRD and XPS. The mechanical properties of the coatings were tested on a standard hardness tester. The tribological behavior of the coatings in dry wear condition was studied by means of ball-on-disc wear test. The experimental results show that addition of copper can restrict the columnar crystal growing to a certain degree. XRD and XPS analysis indicate that coatings are mainly composed of Cr and CrN phase. Cu is mainly existed in a free state in the coatings. Copper adding has no obvious effects on the hardness of the coatings. However, the coatings fracture toughness can be improved by doped copper. The coefficient of friction of the coatings against bearing steel is in the range of 0.25-0.6 changing with the copper content. The coating with 2.6 at% copper shows the lowest coefficient of friction about 0.25 and wear rate which is about one tenth of that of the coating with 6.8 at% copper. The higher coefficient of friction and wear rate of the coating with 6.8at% copper may be attributed to its lower bonding strength.

Effects of Copper Doping on Structure and Properties of Tin Films Prepared by Magnetron Sputtering Assisted by Low Energy Ion Flux Irradiation

Superhard Nc-Tin/Nc-Cu Nanocomposite Film Synthesized by Magnetron Sputtering with Low Energy Ion Flux Irradiation

Influence of Doped Cu-Zn on Structure and Properties of TiN Films

Hard Nanocomposite Ti–Cu–N Films Prepared by D.c. Reactive Magnetron Co-Sputtering

Microstructure and Properties of In-Situ TiC Reinforced Copper Nanocomposites Fabricated Via Long-Term Ball Milling and Hot Pressing

Effect Of Cu Content And Ion Beam Bombardment On Microstructure And Mechanical Properties Of Cr-Cu-N Films

Effect of Cu doping on the microstructure and mechanical properties of AlTiVN-Cu nanocomposite coatings

Microstructure and Tribological Behavior of Cr-Cu-N Coatings Deposited by Ion Beam Assisted Magnetron Sputtering

The effect of zirconium dopant on the properties of copper films

Preparation of Super-Hard Nanocomposite Films by ICP Assisted Magnetron Sputtering

Effects of Ti Doping on the Structures and Magnetic Properties of Films

Properties of Al-doped Copper Nitride Films Prepared by Reactive Magnetron Sputtering

Influence of Cu Content on the Microstructure and Mechanical Properties of Cr-Cu-N Coatings

Preparation of Nanocomposite Thin Films by Ion Beam and Plasma Based Sputtering Processes

Influence of Copper Doping on the Electrical Properties of TaN Thin Films

Effect of Low-Energy Ion Irradiation on Synthesis of Hard and Superhard Films

609 Low-temperature Synthesis of Superhard Nanocomposite Thin Films

Study on the Modification of Tin and Crn Binary Films

The microstructure and mechanical properties of Ti(CoCr)N films produced by DC magnetron sputtering

Cu Doped Ε-Fe2–3n Films with Manipulable Magnetic and Transport Properties

A Comparative Study of Copper-doped and Copper, Nitrogen Co-doped DLC Film Electrode and Its Electrochemical Properties