Synthesis and Catalytic Performance of 2D HZSM-5 Nano-sheet for Ethylbenzene Production from Benzene with Dilute Ethylene
Bian Kai,Hou Zhanggui,Duan Xinrui,Li Xiaoguo,Chang Yang,Cao Hui,Zhang Anfeng,Guo Xinwen
DOI: https://doi.org/10.7503/cjcu20180670
2019-01-01
Abstract:2D HZSM-5 nano-sheet with different b-axis thickness and Si/Al atom ratios were synthesized by seed-induced method under the hydrothermal conditions , using tetrapropylammonium bromide as the template , ethylamine as the mineralizer, , silica sol as the silicon source, aluminium chloride as the aluminium source and the 60 nm silicate-1 as the crystal seed, respectively. And the 2D hierarchical HZSM-5 nano-sheet were obtained by alkaline treatment with different sources, including NaOH treatment, tetrapropylammonium hydroxide (TPAOH) treatment, and NaOH with TPAOH co-alkaline treatment. The structure and acidity of the samples were characterized by means of X-ray diffraction (XRD) , scanning electron microscopy (SEM) , transmission electron microscopy (TEM) , Ar adsorption-desorption , ammonia temperature-programmed desorption(NH3-TPD) , X-ray fluorescence (XRF) and X-ray photoelectron spectroscopy (XPS) . The effects of Si/Al atom ratio and the thickness of b-axis on the alkylation of benzene with dilute ethylene were investigated. The research results show that, under the reaction conditions of 360 degrees C , 1. 4 MPa , the molar ratio of benzene/ethylene is 6 , and the concentration and weight hourly space velocity (WHSV) of ethylene were 15% and 1. 5 h(-1), the conversion of benzene decreased slightly with the increasing of Si/Al atom ratio, the ethyl selectivity maintained above 99. 2%, while the selectivity of toluene and xylene decreased from 0. 11% and 0. 09% to 0. 05%, respectively. The HZSM-5 catalysts with different b-axis thickness were evaluated under the condition of benzene/ethylene is 1, the microscale HZSM-5 with the high silica content deactivated seriously. The conversion of benzene declined from 34. 6% to 8% during 50 h , and the ethyl selectivity was 88%. While the benzene conversion of 2D HZSM-5 nano-sheet with same Si/Al atom ratio was stable at 44. 0%, the ethyl selectivity reached to 94. 8%, and the xylene selectivity reduced from 0. 37% to 0. 22%.