Effect of Y substitution on the high rate dischargeability of AB4.6 alloys as an electrode material for nickel metal hydride batteries
Cheng Tan,Liuzhang Ouyang,Hui Wang,De Min,Canhui Liao,Fangming Xiao,Renheng Tang,Min Zhu
DOI: https://doi.org/10.1016/j.jallcom.2020.156641
IF: 6.2
2020-12-01
Journal of Alloys and Compounds
Abstract:<p>AB<sub>4.6</sub> alloys exhibit excellent high rate dischargeability (HRD) performance but the quick capacity degradation and low discharge capacity restrict application of nickel metal hydride batteries. This study investigated the effect of substituting La with Y on the multiphase structures and overall electrochemical characteristics of the La<sub>0.90-x</sub>Ce<sub>0.08</sub>Y<sub>x</sub>Zr<sub>0.02</sub>Ni<sub>3.91</sub>Co<sub>0.14</sub>Mn<sub>0.25</sub>Al<sub>0.30</sub> (x = 0, 0.3, 0.5, and 0.7) alloys. The results showed that Y tended to form stable [A<sub>2</sub>B<sub>4</sub>] subunit rather than [AB<sub>5</sub>] subunit, thus the Ce<sub>2</sub>Ni<sub>7</sub>-type phase abundance increased from 16.00 wt% to 26.30 wt%, and improved the maximum discharge capacity and hydrogen diffusion. The decrease of i<sub>corr</sub> and particle size demonstrated that the addition of Y enhanced anti-corrosion capability but degraded anti-pulverization capability, where small particles obtained via pulverization were very sensitive to corrosion, thus leading to degradation in discharge capacity. The La<sub>0.6</sub>Ce<sub>0.08</sub>Y<sub>0.3</sub>Zr<sub>0.02</sub>Ni<sub>3.91</sub>Co<sub>0.14</sub>Mn<sub>0.25</sub>Al<sub>0.30</sub> alloy exhibited excellent electrochemical properties, with maximum discharge capacity of 350.4 mAh g<sup>−1</sup>, cycle stability of 80.15% after 100 cycles and HRD of 73.56% (3000 mA g<sup>−1</sup>).</p>
materials science, multidisciplinary,chemistry, physical,metallurgy & metallurgical engineering