Structure and Properties of (K<SUB>0.5</SUB>Na<SUB>0.5</SUB>)<SUB>1-2x</SUB>Sr<SUB>x</SUB>(Nb<SUB>0.94</SUB> Sb<SUB>0.06</SUB>)O<SUB>3</SUB> Lead-free Piezoelectric Ceramics: Structure and Properties of (K<SUB>0.5</SUB>Na<SUB>0.5</SUB>)<SUB>1-2x</SUB>Sr<SUB>x</SUB>(Nb<SUB>0.94</SUB> Sb<SUB>0.06</SUB>)O<SUB>3</SUB> Lead-free Piezoelectric Ceramics

Gui-Fen FAN,Wen-Zhong LV,Yuan-Yuan RAO

DOI: https://doi.org/10.3724/SP.J.1077.2009.00433

IF: 1.292

2009-01-01

Journal of Inorganic Materials

Abstract:Lead-free piezoelectric ceramics (K0.5Na0.5)(1-2x)Sr-x(Nb0.94Sb0.06)O-3 (abbreviated as KNSNS1000x) were synthesized by the conventional ceramic sintering technique. The structure and electrical properties of KNSNS1000x ceramics were investigated. The results of XRD indicate that KNSNS1000x ceramics have ail orthorhombic structure. The proper content of Sr substitute increases the density of ceramics which reaches the maximum value of 4.411 g/cm(3) at x = 0.008. With the increase of the amount of Sr, the T-c decreases and the temperature of orthorhombic-tetragonal phase transition (To-t) is almost a constant. In the temperature range from 0 degrees C to 200 degrees C, dielectric constant of KNSNS1000x ceramics is independent of frequency. The KNSNS8 ceramics obtains the optimum piezoelectric properties: d(33) = 155pC/N, k(p) = 0.361, Q(m) = 120, N-P = 2862, P-r = 23 mu C/cm(2), E-c = 1.4kV/mm, rho = 4.411 g/cm(3).