Abstract:The present article deals with the investigations of the oxidation kinetics of γ-aluminum oxynitride (AlON) in the temperature range of 1173 to 1773K by thermogravimetry. Oxidation experiments with AlON powder and plates have been carried out in air, both in isothermal as well as nonisothermal modes. Oxidation of AlON resulted in the formation of Al2O3. The results showed that the rate of oxidation was negligible below 1273 K and, at higher temperatures, showed an increase with increasing temperature. Both isothermal studies as well as experiments with ramped temperature clearly indicated that the mechanism of the reaction changes around 1600 K. In the nonisothermal mode, the oxidation curve showed a plateau region in this temperature range. The difference between the two reaction steps was explained on the basis of the formation of a metastable alumina phase in the lower temperature region and stable corundum phase at higher temperatures. The buildup of the product layer would lead to a diffusion-controlled reaction kinetics. In the nonisothermal experiments, the phase transformations in alumina product layer at higher temperatures would lead to crack formation, thereby leading to even direct chemical reaction. From the experiments for the isothermal oxidation of AlON powder, the overall activation energy for the reaction rate with chemical control was determined to be 218 kJ/mole in the temperature range of 1273 to 1573 K and 78 kJ/mole in the range of 1573 to 1773 K. The overall activation energy for the diffusion step was found from the isothermal oxidation of AlON plates to be 227 kJ/mole.

Thermodynamic study and synthesis of gamma-aluminum oxynitride

Synthesis, microstructures and properties of γ-aluminum oxynitride

Synthesis, microstructures and properties of gamma-aluminum oxynitride

Structural Characterization of AION by 27 Al Mas NMR and Quantum Chemistry Method

Synthesis of AlON Powder by Aluminothermic Reduction and Its Thermodynamic Analysis

A STUDY ON SYNTHESIS OF AlON BY HOT_PRESS SINTERING

Optical properties of powder and ceramics of aluminium oxynitride obtained by self-propagating high-temperature synthesis

Kinetic Studies of the Oxidation of Γ-Aluminum Oxynitride

Effects of Al2o3 Phase Composition on Alon Powder Synthesis Via Aluminothermic Reduction and Nitridation

Synthesis and Characterisation of Mgalon

Structural characterization of AlON by Al 27 MAS NMR and quantum chemistry method

Oxidation behavior and mechanism of aluminum oxynitride (AlON) at elevated temperatures

Synthesis technology of AlON

Inversion calculation of the interatomic potentials for Ni0.75AlxMo0.25-x alloy employing microscopic phase-field model

Thermodynamic aspects of oxidation for Nb alloying gamma-TiAl intermetallic compounds

Gas‐Phase and Solid‐State Simultaneous Mechanism for Two‐Step Carbothermal AlON Formation

AlON transparent ceramics from powders synthesized by improved direct nitridation

Thermodynamic study and syntheses of β-SiAlON ceramics

Compositional tailoring effect on crystal structure, mechanical and thermal properties of γ-AlON transparent ceramics

Comparative Research of Plasma-Assisted Milling and Traditional Milling in Synthesizing AlN

Synthesis of Ultrafine AlN Powders in an Al-OC-N System