Abstract:The Ni0.5Zn0.5Fe2O4/SiO2 composite nanofibers were prepared using sol-gel process combined with electrospinning. The thermal decomposition and phase inversion process of precursor nanofibers and the effects of calcination temperature and SiO2 content on the phase composition, microstructure, morphology and magnetic property of the resulting nanofibers were studied by means of thermogravimetric and differential thermal analysis, X-ray diffraction, field emission scanning electron microscopy, high resolution transmission electron microscopy and vibrating sample magnetometer. The experimental results show that the cubic spinel structure is basically formed when the precursor nanofibers are calcined at 450 ℃ for 2 h. The average grain size of Ni0.5Zn0.5Fe2O4 contained in the composite nanofibers with 10 % SiO2 and their specific saturation magnetization and coercivity increase with increasing calcination temperature. Amorphous SiO2 additive can effectively restrain the growth of Ni0.5Zn0.5Fe2O4 nanocrystals. As a result, with SiO2 content increasing from 0 to 20 % , the average grain size of Ni0.5Zn0.5Fe2O4 in the prepared Ni0.5Zn0.5Fe2O4/SiO2 composite nanofibers calcined at 900 ℃ for 2 h decreases from 81.6 to 13.3 nm, and the specific saturation magnetization of these samples monotonically decreases, whereas the coercivity initially increases and then decreases due to the change of magnetic domain structure from multi-domain to single-domain along with the reduction in grain size. In addition, with the increase of SiO2 content, the diameter of the as-prepared Ni0.5Zn0.5Fe2O4/SiO2 composite nanofibers gradually increases and the surface becomes smooth.

Magnetic Ni/Sio2 Composite Microcapsules Prepared by One-Pot Synthesis

Controlled Preparation of CoNi2S4 Nanorods Derived from MOF-74 Nanoarrays Involving an Exchange Reaction for High Energy Density Supercapacitors.

Synthesis and Magnetic Properties of Carbon-Coated Ni/SiO 2 Core/shell Nanocomposites

One-pot fabrication of magnetic nanocomposite microcapsules

Preparation of Porous SiO2/Ni/TiO2 Multicoated Microspheres Responsive to Electric and Magnetic Fields

Characterization and Application of Magnetic P (St-Co-maa-co-am)/sio 2 Composite Microspheres

Multi-Functional Thermosensitive Composite Microspheres with High Magnetic Susceptibility Based on Magnetite Colloidal Nanoparticle Clusters

Synthesis of Composite Microgel Capsules by Ultrasonic Spray Combined with in Situ Crosslinking

Preparation and characterization of SiO_2 encapsulated Ni nanoparticles

Preparation of SiO2/(γ-Fe2O3-SiO2 ) Magnetic Catalyst Carrier

Synthesis of Ni-Sio2 Composite Microspheres in Situ in Ethylene Glycol

Facile One-Pot Preparation and Functionalization of Luminescent Chitosan-Poly(Methacrylic Acid) Microspheres Based on Polymer-Monomer Pairs

Synthesis of Monodisperse Fe@SiO2 Core-Shell Nanocapsules and Investigation of Their Magnetic Behaviour

Fabrication and Characterization of Monodisperse Magnetic Porous Nickel Microspheres As Novel Catalysts

One Pot Synthesis of Amino-Functionalized Magnetite/Silica Nanocomposites in Microemulsion

Preparation of One-Dimensional Ni0.5 Zn0.5 Fe2O4/SiO2 Composite Nanostructures and Their Magnetic Properties

Facile One-Pot Assembly of Adhesive Phenol/feiii/pei Complexes for Preparing Magnetic Hybrid Microcapsules

Superparamagnetic high-magnetization composite microspheres with Fe 3 O 4 @SiO 2 core and highly crystallized mesoporous TiO 2 shell

Preparation of uniform magnetic recoverable catalyst microspheres with hierarchically mesoporous structure by using porous polymer microsphere template

Facile Synthesis of Magnetic Microcapsules by Synchronous Formation of Magnetite Nanoparticles

One Pot Soap-Free Synthesis of Fluorescent, Magnetic Composite Particles with High Monodispersity