Abstract:Single-phase Li0.5-0.5xZnxFe2.5-0.5xO4 (where x=0.0, 0.2, 0.3, 0.4, 0.5 and 0.8) nanofibers with diameters of 50 similar to 100 nm were successfully fabricated via electrospinning technique in combination with subsequent heat treatment using polyvinylpyrrolidone, nickel nitrate, zinc nitrate and ferric nitrate as principal raw material. The thermal decomposition process of as-spun precursor nanofibers and the influences of the calcination temperature and chemical composition on the crystal structure, micromorphology and magnetic properties of the prepared nanofiber samples were investigated by means of thermogravimetric and differential thermal analysis, X-ray diffraction, field emission scanning electron microscopy, transmission electron microscopy and vibrating sample magnetometer. The results indicate that the pure crystalline LiZn ferrite nanofibers are basically formed when the precursor nanofibers are calcined at 350 degrees C for 2 h. As the calcination temperature increases from 350 to 600 degrees C, the average grain size of Li0.35Zn0.3Fe2.35O4 nanofibers ranges from 13.0 to 47.5 nm and the micromorphology evolves toward a chain-like structrue. The saturation magnetization of the samples monotonously increases from 39.7 to 84.5 A.m(2).kg(-1), while the coercivity increases initially, reaches a maximun value of 12.6 kA.m(-1) at 550 C and then decreases, which reveals that the magnetic single-domain critical size of Li0.35Zn0.3Fe2.35O4 nanofibers may be around 35 nm. The lattice constant of as-prepared Li0.5-0.5xZnxFe2.5-0.5xO4 nanofibers calcined at 500 degrees C for 2 h exhibits an almost linear increase with increasing x and complies with Vegard's law. The coercivity of these nanofiber samples gradually decreases from 17.1 kA.m(-1) for x=0.0 to 2.4 kA.m(-1) for x=0.8, and the saturation magnetization firstly increases to 74.7 A.m(2).kg(-1) with the value of x up to 0.3 and then decreases beyond this limit. Compared to the nanoparticle counterparts prepared under similar conditions, the LiZn ferrite nanofibers have a relatively high coercivity due to their large shape anisotropy. These LiZn ferrite nanofibers have potential application in many fields such as nanoelectronic devices, sensitive devices, microwave absorbers, and biomedicine.

Mass Synthesis of Nanocrystalline Spinel Ferrites by a Polymer-Pyrolysis Route

Synthesis of Nanocrystalline Spinel CoFe2O4 Via a Polymer-Pyrolysis Route

Synthesis of Nanocrystalline Ferrites Zn0.4ni0.6cr0.5laxfe1.5-Xo4 and Its Magnetic Properties

Synthesis of nanocrystalline Zn0.5Mn0.5Fe2O4 via in situ polymerization technique

Preparation and Characterization of Complex Ferrite Nanoparticles by a Polymer-Pyrolysis Route

Preparation Of Co0.2zn0.2mn0.6fe2o4 Nanoparticles By A Polymer-Pyrolysis Route And Its Characterization

Ferromagnetic Fe3O4 Nanofibers: Electrospinning Synthesis and Characterization

Preparation and Characterization of MnFe2O4 by a Microwave-Assisted Oxidative Roasting Process

Syntheses and Magnetic Properties of Spinel-Type MFe2O4 (M=Ca, Mg, Cu, Zn) Nanocrystalline Powders

Highly Dispersed Spinel (mg, Ca, Ba)-ferrite Nanoparticles: Tuning the Particle Size and Magnetic Properties Through a Modified Polyacrylamide Gel Route

A facile strategy for synthesis of spinel ferrite nano-granules and their potential applications

Microwave-assisted synthesis of spinel ferrite nanospherolites

Study of the Solid-State Synthesis of Nickel Ferrite (NiFe2O4) by X-ray Diffraction (XRD), Scanning Electron Microscopy (SEM) and Raman Spectroscopy

The Chemistry of Spinel Ferrite Nanoparticle Nucleation, Crystallization, and Growth

Synthesis of Nickel-Zinc Ferrite Nanoparticles by the Sol-Gel Auto-Combustion Method: Study of Crystal Structural, Cation Distribution, and Magnetic Properties

Electrospinning Preparation, Structural and Magnetic Properties of Li0.5-0.5xznxfe2.5-0.5xo4 Nanofibers

Large-scale synthesis and characterization of monodisperse Fe3O4 nanocrystals

Magnetic Spinel Ferrite: An Efficient, Reusable Nano Catalyst for HMFsynthesis

A facile synthesis for magnetic ferberite nanostructured material

Surfactant-assisted Synthesis and Magnetic Properties of Monodispersed Manganese Ferrite Nanocrystals

Effects on Direct Synthesis of Large Scale Mono-Disperse Ni0.5zn0.5fe2o4 Nanosized Particles