Abstract:Alumina nanowires were fabricated by high voltage anodization of an aluminum sheet.The formation mechanism was discussed in detail.During the anodization procedure,the microstructure cell array split along the thinnest positions under mechanical stress existing in alumina membranes when the porous alumina membranes grew,thus the alumina nanowires were fabricated.According to the characterizations of scanning electron microscope(SEM)and transmission electron microscope(TEM),the morphologies of separated alumina nanowires are uniform triangular prism with concave and cylindrical side-faces.The alumina nanowires are 30-300 nm in diameter and several to tens of micrometers in length.The specific surface value of brunauerem-mett-teller(BET)measurement is 5.8×104 m2/kg,approximating to the theoretical value of 6.2×104 m2/kg.The experimental results show that these one-dimensional alumina nanostructures have strong absorbability to ultrafine nanoparticles of Ag and CdS.They can absorb nanoparticles(the diameter less than 10 nm)that are too small to be eliminated by conventional filters or centrifuges.Therefore,the as-prepared alumina nanowires will be useful as super absorbents or filters.

Formation of an Array of Isolated Alumina Nanotubes

Formation Mechanism of Alumina Nanotubes and Nanowires from Highly Ordered Porous Anodic Alumina Template

Formation of Si-based Nano-Island Array on Porous Anodic Alumina

Anodizing process of Al films on Si substrates for forming alumina templates with short-distance ordered 25 nm nanopores

Formation mechanism of alumina nanotube array

Individual Alumina Nanotubes Coaxially Wrapping Carbon Nanotubes and Nanowires

In Situ Fabrication of Alumina Nanotube Array and Photoluminescence

Array-orderly single crystalline silicon nano-wires

Fabrication of in Situ Ultrathin Anodic Aluminum Oxide Layers for Nanostructuring on Silicon Substrate

Simultaneous Fabrication of Open-Ended Porous Membrane and Microtube Array in One-Step Anodization of Aluminum

Formation mechanism of individual alumina nanotubes wrapping metal (Cu and Fe) nanowires

In-situ template synthesis of TiO2 nanotube array films

In-situ template synthesis of TiO2 nanotube array films on Al substrates

Hydrophilicity reinforced adhesion of anodic alumina oxide template films to conducting substrates for facile fabrication of highly ordered nanorod arrays

Growth of Well-Aligned Carbon Nanotube Arrays on Silicon Substrates Using Porous Alumina Film As a Nanotemplate

In-Situ Template Synthesis Titania Nanotube Array Films on Aluminum Plate

Titanium oxide nanotube arrays prepared by anodic oxidation

Fabrication of Alumina Nanowires via Anodic Oxidation of Aluminum

Alumina Nanowire Arrays Standing on a Porous Anodic Alumina Membrane

In Situ Template Synthesis of TiO<sub>2</sub> Nanotube Array Films

PREPARATION OF ARRAY FILM OF ALIGNED CARBON NANORODS ON ALUMINUM SUBSTRATE