In-situ influence of TiF 3 catalyst on the hydrogen storage behavior of Mg-Ni-Y based alloy
Hui Yong,Yiwan Chen,Yanquan Ji,Shuai Wang,Jiangwei Ma,Baosheng Liu,Jifan Hu,Yanghuan Zhang
DOI: https://doi.org/10.1016/j.est.2023.110022
IF: 9.4
2023-12-13
Journal of Energy Storage
Abstract:Solid-state magnesium-based hydrogen storage encounters challenges associated with sluggish hydrogen absorption and desorption kinetics. The incorporation of catalysts is considered a promising means to improve the hydrogen absorption and desorption kinetics of these alloys. In this experiment, we prepared the Mg 80 Ni 15 Y 5 alloy via vacuum melting and incorporated TiF 3 in varying weight percentages of 1, 3, 5, and 7 wt% through ball milling . The phase composition and microstructure of the samples were analyzed and measured using X-ray diffraction meter (XRD), Transmission Electron Microscope (TEM), Selected Area Electron Diffraction (SAED), and Scanning Electron Microscope (SEM) techniques. The results revealed that the TiF 3 introduced two catalytically phases, MgF and TiF 2 . And TiF 2 transforms into TiH 2 after hydrogen absorption, which covers the surface of MgH 2 and prolongs the nucleation time of MgH 2 .Furthermore, the addition of TiF 3 made the surface of alloy markedly coarser and more irregular and few cracks, providing channels for hydrogen diffusion. This behavior optimized the kinetic performance of the alloy. It was observed that the samples containing 7 wt%TiF 3 achieved 99.2 % hydrogen saturation even in low-temperature. It's worth mentioning that the addition of 7 wt% TiF 3 to the Mg 80 Ni 15 Y 5 alloy significantly reduced the dehydrogenation activation energy to 58.5 kJ/mol, as opposed to pure magnesium with an activation energy of 158.2 kJ/mol. This substantial reduction has effectively accelerated the hydrogen absorption and desorption rates of the alloy. However, it had only a negligible impact on the thermodynamic properties of the sample with 7 wt%TiF 3 .
energy & fuels