Abstract:Development of metallic glasses is hindered by the difficulties in manufacturing bulk parts large enough for practical applications. Spark plasma sintering (SPS) has emerged as an effective consolidation technique in the formation of bulk metallic glasses (BMGs) from melt-spun ribbons. In this study, Mg65Zn30Ca5 melt-spun ribbons were sintered at prolonged sintering times (15 min to 180 min) via SPS under a pressure of 90 MPa and at a temperature of 150 °C (which is below the crystallization temperature), to provide an insight into the influence of sintering time on the consolidation, structural, and biodegradation behavior of Mg-BMGs. Scanning Electron Microscopy was used to characterize the microstructure of the surface, while the presence of the amorphous phase was characterized using X-ray diffraction and Electron Backscatter Diffraction. Pellets 10 mm in diameter and height with near-net amorphous structure were synthesized at 150 °C with a sintering time of 90 min, resulting in densification as high as 98.2% with minimal crystallization. Sintering at extended durations above 90 min achieved higher densification and resulted in a significant amount of local and partial devitrification. Mechanical properties were characterized via compression and microhardness testing. Compression results show that increased sintering time led to better structural integrity and mechanical properties. Notably, SPS150_90 displayed ultimate compressive strength (220 MPa) that matches that of the cortical bone (205 MPa). Corrosion properties were characterized via potentiodynamic polarization with Phosphate Buffered Solution (PBS). The results suggest that the sintered samples have significantly better corrosion resistance compared to the crystalline form. Overall, SPS150_90 was observed to have a good balance between corrosion properties (10× better corrosion resistance to as-cast alloy) and mechanical properties.

Fabrication of ZrCuAlNi Metallic Glassy Matrix Composite Containing ZrO2 Particles by Spark Plasma Sintering Process

Fabrication of Nanocrystalline Zro2 Particle Reinforced Aluminum Alloy Composite by Squeeze Casting Route

Powder metallurgy process enables production of high-strength conductive Cu-based composites reinforced by Cu50Zr43Al7 metallic glass

Microstructure and Mechanical Properties of Composites Obtained by Spark Plasma Sintering of Al–Fe66Cr10Nb5B19 Metallic Glass Powder Mixtures

Microstructure and mechanical behavior of metallic glass fiber-reinforced Al alloy matrix composites

Optimizing mechanical and electrical properties of Cu-coated Cu–Zr–Al bulk metallic glass composites by adjusting glassy powder size

ZrO 2 Strengthened NiAl/Cr（Mo,Hf） Composite Fabricated by Powder Metallurgy

Preparation and interfacial bonding of oversize ZrO2 reinforced metal matrix composites prepared by spark plasma sintering

Fabrication and Characteristic of 2024al Matrix Composites Reinforced by Carbon Fibers and ZrCp by Spark Plasma Sintering

Metallic Iron or a Fe-Based Glassy Alloy to Reinforce Aluminum: Reactions at the Interface during Spark Plasma Sintering and Mechanical Properties of the Composites

Synthesis of Bulk Zr48Cu36Al8Ag8 Metallic Glass by Hot Pressing of Amorphous Powders

Effects of Crystallization Fractions on Mechanical Properties of Zr-based Metallic Glass Matrix Composites

Mechanical and corrosion properties of Ti-Ni-Cu-Zr metallic glass matrix composites

Towards a Better Understanding of the Interaction of Fe66Cr10Nb5B19 Metallic Glass with Aluminum: Growth of Intermetallics and Formation of Kirkendall Porosity during Sintering

Plasticity-improved Zr–Cu–Al Bulk Metallic Glass Matrix Composites Containing Martensite Phase

Formation of Nanoscale Metallic Glassy Particle Reinforced Al-Based Composite Powders by High-Energy Milling

Microstructure and Mechanical Properties of Nano-Size Zirconium Carbide Dispersion Strengthened Tungsten Alloys Fabricated by Spark Plasma Sintering Method

Heat Treatable Al‐Zn‐Mg‐Cu Matrix Composites Reinforced With Ni‐Based Metallic Glass Powder

Enhancing Mechanical and Biocorrosion Response of a MgZnCa Bulk Metallic Glass through Variation in Spark Plasma Sintering Time

Heterogeneous metallic glass composites with a unique combination of strength, plasticity and conductivity

Improved strength and conductivity of metallic-glass-reinforced nanocrystalline CuCrZr alloy