Preparation and Performance of Ni Nano-particle Doping with Pt for Methanol Electrocatalytic Oxidation
SONG Hui,ZHANG Zhong-lin,LI Yi-bing,DUAN Dong-hong,LIU Shi-bin,HAO Xiao-gang,H SONG,Y LI,S LIU,X HAO
2010-01-01
Abstract:Ni-Pt/C(Pt mass fraction of 5%),which is Ni-based binary metal nano-particle electro-catalyst used in anion exchange membranes direct methanol fuel cell,was prepared by sol-gel method.The effects of catalyst preparation conditions,such as the amount of reducing agent,on performance of NiPt/C for methanol electrocatalytic oxidation were investigated by cyclic voltammetry,and the morphology,crystalline structure and composition of particle surface were characterized by transmission electron microscopy(TEM),X-ray diffraction(XRD) and X-ray photoelectron spectroscopy(XPS).The results show that,the diameter of Ni-Pt nano-particles with face-center-cubic structure(fcc) was about 4~6 nm,the Pt and Ni atomic ratio of surface was higher than that of the bulk,with the increase in the amount of reducing agent and the calcination temperature,the catalytic activity increased at first and then decreased,the optimum reductant dosage was 1.2 times the theoretical value,the best calcination temperature was 400℃,when Ni and Pt precursors for the catalysts were reduced at the same time,Ni-Ptalloy/C had the highest catalytic activity.