Abstract:The multiple melting behavior of poly(ethylene terephthalate) (PET) homopolymers of different molecular weights and its cyclohexylene dimethylene (PET/CT) copolymers was studied by time-resolved simultaneous small-angle X-ray scattering/wide-angle X-ray scattering diffraction and differential scanning calorimetry techniques using a heating rate of 2°C/min after isothermal crystallization at 200°C for 30min. The copolymer containing random incorporation of 1,4-cyclohexylene dimethylene terephthalate monomer cannot be cocrystallized with the ethylene terephthalate moiety. Isothermally crystallized samples were found to possess primary and secondary crystals. The statistical distribution of the primary crystals was found to be broad compared to that of the secondary crystals. During heating, the following mechanisms were assumed to explain the multiple melting behavior. The first endotherm is related to the non-reversing melting of very thin and defective secondary crystals formed during the late stages of crystallization. The second endotherm is associated with the melting of secondary crystals and partial melting of less stable primary crystals. The third endotherm is associated with the melting of the remaining stable primary crystals and the recrystallized crystals. Due to their large statistical distribution, the primary crystals melt in a broad temperature range, which includes both second and third melting endotherms. The amounts of secondary, primary and recrystallized crystals, being molten in each endotherm, are different in various PET samples, depending on variables such as isothermal crystallization temperature, time, molecular weight and co-monomer content.

Thermoreversible Gel Formation in Poly(Ethylene Terephthalate)/Epoxy Resin Solutions

Morphology And Molecular Motion Of Poly(Ethylene Terephthalate) In Polymer/Oligomer Gel

Viscoelastic Effects on the Phase Separation in Thermoplastics-Modified Epoxy Resin

Rheological Behaviors and Structural Transitions in A Polyethersulfone-Modified Epoxy System During Phase Separation

Thermo-reversible Gelation of Atactic Poly(methyl Methacrylate) in Poly(ethylene Glycol) Oligomers

Gelation Behavior of Thermoplastic-Modified Epoxy Systems During Polymerization-Induced Phase Separation

Miscibility and Interchange Reactions in Blends of Bisphenol-A-Type Epoxy Resin and Poly(Ethylene Terephthalate)

On the Nature of Multiple Melting in Poly(Ethylene Terephthalate) (pet) and Its Copolymers with Cyclohexylene Dimethylene Terephthalate (Pet/ct)

Translating Thermal Response of Triblock Copolymer Assemblies in Dilute Solution to Macroscopic Gelation and Phase Separation

Thermal Reversible Gelation During Phase Separation of Poly(n-Isopropyl Acrylamide)/water Solution

Nonisothermal Crystallization of Recycled Poly(Ethylene Terephthalate)/Poly(Ethylene Octene) Blends

In Situ Formation and Gelation Mechanism of Thermoresponsive Stereocomplexed Hydrogels upon Mixing Diblock and Triblock Poly(Lactic Acid)/Poly(Ethylene Glycol) Copolymers.

Complexation of Poly(ethylene Glycol) with Poly(ethyl Methacrylate-Co-n-vinyl-2-pyrrolidone) Gel Based on Hydrogen Bonds

Properties and Mechanism of Crystallization and Cold Crystallization of PET/PEN Blends

Polycondensation Reaction of P-Acetoxybenzoic Acid and Poly(Ethylene Terephthalate) and the Formation of Ether Bonds

Non-isothermal Crystallization Behavior of Poly(ethylene Terephthalate)/poly(trimethylene Terephthalate) Blends

Phenylethynyl-Terminated Imide Oligomer-Based Thermoset Resins

Concentration Dependence of Crystalline Poly(Ethylene Terephthalate) Prepared by Freeze-Extracting Solutions

In-situ polymerization-modification process and foaming of poly(ethylene terephthalate)

Phase diagram for the gelation of temperature-responsive and biocompatible poly(oligo ethylene glycol methyl ether methacrylate) polymers in aqueous free-radical polymerization reactions

Large‐Scale Fluctuation Behavior Prior to the Crystallization of Poly(ethylene terephthalate) Glass: A Small‐Angle Light Scattering Study