Construction of cartilage tissue engineered scaffold by rabbit bone marrow mesenchymal stem cells/chitosan-collagen composite
Dianwei W. Chu,Wei Wang,Chen Li-jun,Wang Wen-liang,Hualiang Liang Zhang,Liang Yang,Li Jian-xin
DOI: https://doi.org/10.3969/j.issn.1673-8225.2009.42.010
2009-01-01
Abstract:BACKGROUND: The core of cartilage tissue engineering is that a few of cells following in vitro culture and amplification are attached to three-dimensional porous scaffold, and cell/scaffold composite is then implanted to form new tissues. OBJECTIVE: To study the feasibility of rabbit bone marrow mesenchymal stem cells (BMSCs)/chitosan-collagen scaffolds to considered as cartilage tissue engineered scaffold. DESIGN, TIME AND SETTING: An in vitro cell-scaffold observation was performed at Research Room of Biochemistry, Medical College of Chinese People's Armed Police Force from March 2008 to February 2009. MATERIALS: Six Japanese rabbits were used for separation and culture BMSCs. Chitosan was provided by Aokang Biotechnology Co., Ltd., Shangdong; type I collagen was provided by Sigma, USA. METHODS: 3% chitosan and 2%collagen were mixed in acetic acid solution, and the mixture was then put in 72-well plate, pre-frozen at -20 °C for 10 hours, and frozen and dried for 24 hours to obtain chitosan-collagen scaffold. The third-passage rabbit BMSCs were inoculated in the scaffold at the density of 1×109/L to construct cell/scaffold composite. MAIN OUTCOME MEASURES: Physico-chemical properties of scaffold were detected using Fourier transform infrared spectroscopy, scanning electron microscopy, and liquid substitution method, while cell growth was observed after three-dimensional culture. RESULTS: Pore of chitosan-collagen scaffold was 160-380 μm, with the mean value of 270 μm. the permeability was well, and the porosity was (86.00±5.12)%. Fourier transform infrared spectroscopy indicated that the products in the cell/scaffold composite group contained chitosan and collagen peaks, but polyethylene glycol peak was not found. At 24, 48, and 72 hours after cell/scaffold co-culture, BMSCs permeated into porous structure of the scaffold and adhered to the scaffold. Partial BMSCs were in fusion with the scaffold. CONCLUSION: The novel chitosan-collagen scaffold is satisfactory for cartilage tissue engineered scaffold, thus it can be used as a vector of seed cells.