Abstract:To improve the dispersion stability of carbon black in water,the grafting of water-soluble polymer poly-(sodium 4-styrenesulfonate) (PSS) onto carbon black (CB) was achieved by the radical polymerization of the corresponding monomers in the presence of CB under ultrasonic irradiation.This technique could generate efficient polymerization of sodium 4-styrenesulfonate (NaSS) in the presence of CB in a rapid reaction at relatively low temperature.The grafted amount of polymer on CB was assessed by thermogravimetric analysis (TGA).In addition,molecular weight and molecular weight distribution of the un-grafted polymer was tracked by gel permeation chromatography (GPC).The influences of ultrasonic time and power output on grafting ratio were also investigated.Fourier transform infrared spectroscopy (FT-IR) was used to determine the chemical structure of the resulting products.Particle analysis indicated that the diameters of the obtained grafted carbon black (GCB) particles were smaller than those of original CB particles.TEM photographs showed that PSS were attached on the surface of carbon black, and the conglomeration degree of GCB decreased apparently.The results of zeta potential measurements revealed that the GCB surface had more negative charges than the original CB.Accordingly,UV transmission measurements conformed that the dispersion stability of GCB in water was improved apparently than that of initial CB.Because of the attachment of polyelectrolyte to the CB surface the grafted CB could be well dispersed in water.

Grafting Modification of Carbon Black by Trapping Macroradicals Formed by Sonochemical Degradation

Bulk Graft Modification of Polyolefin Membranes by Combining Pre-Irradiation-Induced Graft and Supercritical Co2-Swelling Polymerization

Polymer Grafting Onto Carbon Black by Solid State Method

Novel Comb‐structured‐polymer‐grafted Carbon Black by Surface‐initiated Atom Transfer Radical Polymerization and Ring‐opening Polymerization

Controlled Grafting of Comb Copolymer Brushes on Poly(tetrafluoroethylene) Films by Surface-Initiated Living Radical Polymerizations.

Grafting polymers onto carbon black surface by trapping polymer radicals

Modification of Carbon Black Through Grafting Multihydroxyl Hyperbranched Polyether Onto Its Surface

Preparation and Characterization of Poly(methyl Methacrylate) and Poly(maleic Anhydride-Co-diallyl Phthalate) Grafted Carbon Black Through Γ-Ray Irradiation

PREPARATION OF POLY (SODIUM 4-STYRENESULFONATE) GRAFTED CARBON BLACK Via ULTRASONIC IRRADIATION INITIATED RADICAL POLYMERIZATION

Recent Research Progress on Polymer Grafted Carbon Black and Its Novel Applications

Preparation Of Polymer-Grafted Carbon Black Nanoparticles By Surface-Initiated Atom Transfer Radical Polymerization

Influence of In-situ Grafting on the Dispersion of Carbon Black in Solvents and Natural Rubber

DISPERSION OF in Situ GRAFTED CARBON BLACK WITH NATURE RUBBER

Grafting Modification and Structural Degradation of Multi-Walled Carbon Nanotubes under the Effect of Ultrasonics Sonochemistry.

Grafting of Maleic Anhydride Onto Carbon Black Surface Via Ultrasonic Irradiation

Preparation and Characterization of Water-Dispersible Carbon Black Grafted with Polyacrylic Acid by High-Energy Electron Beam Irradiation

Preparation of Nano-Carbon Black Particles by Grafted with Small Organic Molecule in Supercritical CO2 and Its Reinforcing Effect to Rubber

A Temperature-Responsive Carbon Black Nanoparticle Prepared by Surface-Induced Reversible Addition–fragmentation Chain Transfer Polymerization

Cationic Grafting from Carbon Black. IX. Cationic Ring-Opening Polymerization and Copolymerization of 3,3-Bis-(chloromethyl)oxetane Initiated by Acylium Perchlorate Groups on Carbon Black

Effect of Surface Modifications of Carbon Black (CB) on the Properties of CB/polyurethane Foams

Cationic Grafting from Carbon Black VI. Grafting of Polyetheresters from Carbon Black by Cationic Ring-Opening Terpolymerization of Tetrahydrofuran-Cyclic Acid Anhydrides-Epichlorohydrin