Abstract:Twin roll casting has been used to produce sheet of Mg60Cu29Gd11 bulk metallic glass (BMG). Sheet can be produced with thicknesses between 1 and 4 mm, the width of sheet produced can be between 25 and 75 mm. The dimensional stability of the produced sheet in a cast run is ±1 mm in the width direction and ±0.05 mm in the thickness direction. As with all magnesium-based BMGs the sheet produced is strong yet brittle at room temperature. The maximum flexural stress of a twin roll cast Mg60Cu29Gd11 BMG strip is 150 MPa with a flexural strain of 0.005. The Charpy impact energy of a Mg60Cu29Gd11 BMG strip is 0.02 J. In order to improve the toughness values of the Mg60Cu29Gd11, BMG strip laminates of BMG and aluminum alloy (UNS A91100) were produced via roll bonding. The introduction of aluminum layers to the sheet structure provides a barrier to shear band movement stopping the sudden catastrophic failure of the sheet. After rolling the BMG was examined via X-ray diffraction (XRD) to confirm that the BMG layer remained amorphous. The flexural stress, flexural strain, and Charpy impact energy properties of BMG-Al laminates are improved when compared to monolithic glass properties. The flexural stress values for laminates compared to the monolithic glass improve by 60 pct from 150 to 250 MPa. The flexural strain values improve by over an order of magnitude from 0.005 to 0.14. The Charpy impact energies increase by 2 orders of magnitude from 0.02 to 2.5 J.

Formation and Mechanical Properties of Mg-Cu-Al-Gd Bulk Metallic Glass Composites

Effect of Al addition on properties of Cu45Zr45.5Ti9.5 bulk metallic glass

Crystallization Behavior and Mechanical Properties of Cu-based Bulk Metallic Glass Composites

Glass Formability, Thermal Stability and Mechanical Properties of La-Based Bulk Metallic Glasses

Structural and mechanical characterizations of ductile Fe particles-reinforced Mg-based bulk metallic glass composites

Formation and mechanical properties of Cu_(58)Zr_(20)Ti_(20)Mo_2 bulk metallic glass

Preparation of Carbon-nanotube Reinforced Mg Based Bulk Metallic Glass Composites and Its Mechanical Properties

Effects of Al on Glass-Forming Ability and Thermal Stability of Cu-Based Metallic Glass

Plasticity-improved Zr–Cu–Al Bulk Metallic Glass Matrix Composites Containing Martensite Phase

Optimizing mechanical and electrical properties of Cu-coated Cu–Zr–Al bulk metallic glass composites by adjusting glassy powder size

Microstructure and mechanical behavior of metallic glass fiber-reinforced Al alloy matrix composites

Cu-Zr-Al-Ti bulk metallic glass with enhanced glass-forming ability, mechanical properties, corrosion resistance and biocompatibility

Glass Forming Ability and Corrosion Resistance of Zr-Cu- Ni-Al-Ag Bulk Metallic Glass

Mechanical Behavior of Carbon Nanotube-Reinforced Mg–Cu–Gd–Ag Bulk Metallic Glasses

The Correlation among the Atomic Structure, Electronic Valence Band and Properties of Zr-Cu-Al-Ag Bulk Metallic Glasses

Zr–(Cu,Ag)–Al Bulk Metallic Glasses

Centimeter-sized Ti-based Bulk Metallic Glass with High Specific Strength

Close Correlations among Thermodynamic, Structural and Mechanical Properties in Mg-Cu-Y Metallic Glasses

Production and Mechanical Properties of Roll Bonded Bulk Metallic Glass/Aluminum Laminates

Atomic Structure and Glass Forming Ability of Cu46zr46al8 Bulk Metallic Glass

Atomic Structure in Al-Doped Multicomponent Bulk Metallic Glass