Determination of freeze-dried and irradiated porker dural resistant ability to collagenase digestion and biomechanics
You-lai Zhang,Yuan-lin Zeng,Guo-hua Xin
DOI: https://doi.org/10.3321/j.issn:1673-8225.2008.41.024
2008-01-01
Abstract:Background: Ideal dural substitute materials requires its good biomechanics properties, tenacity and elasticity. Objective: To determine freeze-dried and irradiated porker dura's resistant ability, including type I collagenase digestion, the biggest load and tensile strength, to assess the porker's dura irradiated and freeze-dried whether or not can satisfy the biomechanics requirment in dura draft. Design, Time and Setting: This controlled analysis experiment was performed at the Burn Institute, Nanchang University, Association Mechanics Laboratory, Nanchang University-New Sans Company,Chinese Crude Drug Solid Preparation Nation Project Research Center of Jiangxi Traditional Chinese Medical College and Jiangxi Tianzhao Technology Development Company from July 2007 to June 2008. Materials: Six healthy living pigs was used to sterilely obtain fresh dura mater. Methods: After washing, pre-frozen, freeze-dried and radiation by 60Co γ-ray, we prepared fresh, freeze-dried, irradiated and freeze-dried plus irradiated pig dura. Main Outcome Measures: 5-mm wafer of four group dura were dealt with type I collagenase meanwhile, digested time was recorded. EMT color screen electronic testing machine was used to measure the biggest load and tensile strength of the porker dura in each group. Results: Time of the dura resistance to collagenase digestion were respectively (8.3±2.5), (7.6±1.8), (23.6±5.7) and (21.1± 5.3) minutes, and the largest load and tensile strength were (79.93±4.36), (70.50±5.97), (96.97±4.84) N and (93.59±4.61), (7.98±0.44), (7.05±0.60), (9.70±0.48) and (9.40±0.46) N/mm in the fresh, freeze-dried, irradiated, and freeze-dried plus irradiated pig dura groups. Compared with the fresh and freeze-dried pig dura groups, the time was longer in the irradiated and freeze-dried plus irradiated pig dura groups (P < 0.05). However, there was no significant difference between the irradiated and freeze-dried plus irradiated pig dura groups (P > 0.05). Conclusion: Dural substitute materials irradiated by 60CO γ-ray enhanced the ability against enzymatic hydrolysis and biomechanics. Irradiated and freeze-dried plus irradiated dural substitution can meet the requirements of the biomechanics in dura mater transplantation.