Abstract:Low-cycle fatigue (LCF) behavior of nickel-based precipitation-strengthened superalloy GH4145/SQ was investigated systematically under fully reversed total strain amplitude control conditions at 538°C in laboratory air. It was shown that the alloy exhibited a pronounced initial fatigue hardening followed by continuous fatigue softening to failure at high strain amplitudes, while at low strain amplitudes the initial hardening was followed by a well-defined saturation stage. Microstructure observations using optical and transmission-electron microscopy revealed that slip band density increased with increasing total strain amplitudes and the size of the γ′precipitates tended to reduction due to repeated shearing by the dislocations with continuous cyclic straining. The above changes in microstructures during cycling were essentially responsible for the fatigue hardening–softening behavior of the alloy. Both optical and SEM micrographs indicated that at low strain amplitudes crack propagation was basically transgranular, while at high strain amplitudes crack propagation was essentially intergranular. Bilinear behavior with a change of slope at a plastic strain amplitude of about 0.2pct was observed in cyclic stress–strain (CSS), Coffin–Manson (C–M) and plastic strain energy–life plots. A change in the number of operating slip systems and the fracture modes with the strain amplitude employed was used to explain this two-slope characteristic. In both the companion specimens test (CST) and the incremental step test (IST) methods the alloy exhibited non-masing type behavior. It was suggested that, for the first approximation, the half-life plastic strain energy could be calculated directly according to the equation without reckoning in the non-masing behavior.

Gigacycle Fatigue Behaviors of Two Sncm439 Steels with Different Tensile Strengths

Low cycle fatigue behavior of nickel-based superalloy GH4145/SQ at elevated temperature

Effect of cyclic straining at elevated-temperature on static mechanical properties, microstructures and fracture behavior of nickel-based superalloy GH4145/SQ

Micro-Defect Effect on Gigacycle Fatigue S-N Property and Very Slow Crack Growth of High Strength Low Alloy Steel

GIGACYCLE FATIGUE OF ULTRA-HIGH STRENGTH STEELS

Gigacycle fatigue in high strength steels

Low Cycle Fatigue Behavior of Original Ferritic P92 Steel at High Temperature: Experiments and Simulations

Comparative Study of High-Cycle Fatigue and Failure Mechanisms in Ultrahigh-Strength CrNiMoWMnV Low-Alloy Steels

Low Cycle Fatigue and Creep Fatigue Interaction Behavior of 9Cr-0.5Mo-1.8w-v-nb Heat-Resistant Steel at High Temperature

Roles of microstructures in high-cycle fatigue behaviors of 42CrMo high-strength steel under near-yield mean stress

Influence of Inclusion Size on Fatigue Behavior of High Strength Steels in the Gigacycle Fatigue Regime

Gigacycle Fatigue Behavior of 1800 MPa Grade High Strength Spring Steel for Automobile Lightweight

Characterization of the Cyclic Softening and Remaining Creep Behaviour of P92 Steel Weldment

Ultra High Cycle Fatigue Behavior of Automotive High Strength Spring Steels 54sicrv6 and 54Sicr6

High-Cycle Fatigue Fracture Behavior of Ultrahigh Strength Steels

Microstructure evolution and very-high-cycle fatigue crack initiation behavior of a structural steel with two loading intermittence modes

The Effect of Stress Ratios on the Very High Cycle Fatigue Behavior of 9%Cr Turbine Steel at 630 °C

High-Cycle, Low-Cycle, Extremely Low-Cycle Fatigue and Monotonic Fracture Behaviors of Low-Carbon Steel and Its Welded Joint

Very High Cycle Fatigue Behaviour of 2000‐mpa Ultra‐high‐strength Spring Steel with Bainite–martensite Duplex Microstructure

Surface Vs. Interior Failure Behaviors in a Structural Steel under Gigacycle Fatigue: Failure Analysis and Life Prediction