Abstract:Photoluminescence (PL) and resonance Raman spectroscopy are used to track changes in the conformations and packing of poly-(2-methoxy-5-(3'-7'-dimethyloctyloxy)-1,4-phenylenevinylene) (MDMO-PPV) chains with the addition of [6,6]-phenyl-C(61)-butyric acid methyl ester (PCBM) molecules. PL lineshapes of MDMO-PPV thin films as a function of annealing time were first measured to determine the spectroscopic signatures of chain conformations and packing in the absence of PCBM. Annealing results in enhanced interchain interactions leading to red-shifts of PL 0-0 transitions by up to ∼300 cm(-1) and apparent increases of the line shape Huang-Rhys factors. Wavelength-dependent PL lifetimes of as-cast and films annealed for short times (∼30 s) are nonexponential with an instrument-limited component of ∼100 ps and a ∼350 ps component. With longer annealing times, decays become single exponential with an average lifetime of ∼1 ns indicating that all excitations efficiently funnel to strongly coupled interchain sites. Addition of PCBM disrupts MDMO-PPV interchain interactions causing PL 0-0 transitions to blue-shift, increases in line width, and decreases in apparent Huang-Rhys factors. Resonance Raman spectra of MDMO-PPV/PCBM thin films with variable PCBM weight fractions (∼50:1 up to 1:8 w/w) were then measured using short (488 nm) and long (568 nm) excitation wavelengths. The out-of-plane vinylene C-H wag mode of MDMO-PPV (∼964 cm(-1)) showed pronounced increases in intensity of up to ∼30% and red-shifts of up to 5 cm(-1) with increasing PCBM content. These changes result from a decrease of planarity between chain segments that suppresses interchain interactions. Furthermore, red-shifts of up to ∼4 cm(-1) were observed for the C═C symmetric stretch of the MDMO-PPV vinylene group (∼1625 cm(-1)) with 488 nm excitation. The sensitivity of the MDMO-PPV vinylene group vibrations with PCBM indicates preferential interactions between these two molecules and is consistent with intercalation of PCBM into the polymer structure. This assignment was confirmed by thermally annealing of MDMO-PPV/PCBM films to remove intercalated PCBM molecules, which partially restores interchain interactions as seen from smaller intensity increases (∼15%) and red-shifts (∼2 cm(-1)) of the ∼964 cm(-1) mode. Overall, the spectroscopic results show that MDMO-PPV chains adopt distorted conformations (i.e., less intrachain order and shorter conjugation lengths) that have important implications for explaining the structural origins for large improvements in charge mobilities in MDMO-PPV/PCBM blends.

Temperature Dependence of Photoluminescence in MEH-PPV Blend Films

Temperature-dependent Photoluminescence from MEH-PPV and MEH-OPPV Containing Oxadiazole in the Main Chain

Effect of Thermal Annealing on Aggregations in MEH-PPV Films

Effects Of Thermal Annealing On Photoluminescence Spectra In Pi-Conjugated Polymer Film: Evidence For Dual Emission By Temperature Dependent Measurements

Optical Emission from the Aggregated State in Poly [2-Methoxy-5-(2′-ethyl-hexyloxy)-p-phenylene Vinylene]

Aging of Poly(2-methoxy-5-(2‘-ethylhexyloxy)-1,4-phenylenevinylene)/Toluene Solutions and Subsequent Effects on Luminescence Behavior of Cast Films

Effect of thermal annealing in atmosphere on photoluminescence of BTEO-PPV films

Spectral Properties of Porphyrin Doped MEH-PPV As Films and in Chloroform Solutions

Temperature Effect On The Electronic Spectra Of Poly(P-Phenylenevinylene)

Improved Device Efficiency and Color Purity: Spectral Redshift and Line Narrowing for Poly [2-Methoxy,5-(2-ethylhexyloxy)-1,4-phenylenevinylene] Via Blending with Phenyl-Substituted Poly [P-Phenylene Vinylene] Derivatives

Effect of Ultrasonication on Optical Properties and Electronic States of Conjugated Polymer Meh-Ppv

Photo- and Electro-Luminescent Properties of 5,10,15,20-Tetra-p-tolyl-21h,23h-porphine Doped Poly[2-Methoxy-5-(2′-ethylhexyloxy)-1,4-phenylenevinylene] Films

Effect of Thermal Annealing on Conformation of MEH-PPV Chains in Polymer Matrix: Coexistence of H- and J-Aggregates

Blue Electroluminescence Mechanism of Polyester Derivative Blend Films

Enhanced Exciton Migration in Electrospun Poly[2-Methoxy-5- (2′-Ethylhexyloxy)-1,4- Phenylenevinylene]/poly(vinyl Pyrrolidone) Nanofibers

Mechanical and Thermal Properties of Poly(Phthalazinone Ether Sulfone)/Poly(Ether Sulfone) Blends

Effect of fullerene intercalation on the conformation and packing of poly-(2-methoxy-5-(3'-7'-dimethyloctyloxy)-1,4-phenylenevinylene)

Temperature-Dependent Luminescence Originating from the Recombination of Excitons in Organic Light-Emitting Materials

Solid-state electrochemical investigation of poly[2-methoxy, 5-(2′-ethyl-hexyloxy)-1,4-phenylene vinylene]

ENERGY TRANSFER AND EXCITON SPATIAL CONFINEMENT IN COPOLYMERS AND BLENDS BASED ON POLYBENZAZOLES

Temperature-Dependent Photoluminescence Of Organic Light-Emitting Materials: Types Excitons Involved In The And Characteristics Of Emitting Process