Controllable Growth of Nbte4 Micro/Nanostructures on Nb Substrates and Their Field-Emission Performance

Xingcai Wu,Yourong Tao,Qixiu Gao,Yuling Zhang

DOI: https://doi.org/10.1039/b820654f

2009-01-01

Journal of Materials Chemistry

Abstract:Single-crystalline NbTe4 microcone, microplate, and nanorod arrays were grown on Nb substrates by a surface-assisted chemical-vapor-transport under different conditions. The microcones are composed of small and large cones with a bending top. The small cones have a top diameter of about 0.2 µm, a bottom diameter of about 1.2 µm, and a length up to approx. 7.7 µm. The large cones originate from self-assembled small cones. The microplates mostly stand on Nb foils, with a diameter of about 2–3 µm and a thickness from 50 to 250 nm. The nanorods have a rectangle section of 250 × 150 to 250 × 250 nm2 or a triangle section with a side of about 250 nm, and a length up to 4.5 µm, partly standing on the substrates. Their growth mechanisms are briefly discussed. Field-emission experiments showed that the three micro/nanostructures have a notable emission current, and their turn-on fields (defined as the electric field required to produce a current density of 10 µA cm−2) are 4.7, 2.0, and 1.9 V µm−1, respectively, suggesting their potential application in electron emission devices.