Abstract:Impact properties of carbon/kevlar composites schematic diagram. In this article, carbon/kevlar hybrid composites were prepared using Vacuum Assisted Resin Infusion (VARI). The sandwich structure with plain carbon weave fabric as the core layer and plain kevlar weave fabric as the surface layer was selected as reinforcement and the solution of epoxy resin and curing agent was selected as matrix. The low velocity impact experiment and compression after impact (CAI) experiment were carried out on the samples at different hybrid ratio and different temperatures, and the mechanical response on the impact loads were analyzed respectively. The results show that the specimen can limit the delamination defect expansion of the surface kevlar fiber as the carbon fiber used as the core layer, which reduce the delamination defect area and improve the impact resistance of the sample. The toughness of the sample improves the brittle failure mode, that is, the sample still has a certain bearing capacity after the load exceeds the maximum strength, the sandwiched composites presents a positive hybrid effect. With the increase of temperature, the matrix was obviously softened, the macromolecular movement in the system was intensified, the three‐dimensional network macromolecular structure of the matrix and the fiber/matrix interface properties were damaged, and the mechanical properties showed an obvious downward trend. As far as the influences of hybrid ratio and temperature on impact behavior of composite are concerned, it lay a theoretical foundation for the industrial application of carbon/kevlar hybrid composites. Highlights The sandwiched structure was used to design the composites, which greatly improves the impact properties of the specimens. The impact properties and compression after impact properties at different hybrid ratios and different temperatures were studied. Based on the hybrid effect and temperature effect, the impact failure mechanism of the sample was analyzed.

Study of Dynamic Impact Behaviors and Ballistic Properties of Hybrid Composites

Impact response and damage evolution of triaxial braided carbon/epoxy composites. Part I: Ballistic impact testing

STUDY ON DAMAGE MECHANISM OF PLAIN WEAVE COMPOSITE UNDER HIGH VELOCITY IMPACT

Thickness effect on ballistic impact behavior of hybrid carbon/Kevlar composites

Study of Dynamic Impact Behaviors and Ballistic Properties of Ceramic/UHMWPE Composite Armor

Investigations of the ballistic response of hybrid composite laminated structures

Finite Element Study on the Impact Resistance of Laminated and Textile Composites.

Hybridization Effects on Ballistic Impact Behavior of Carbon/ Aramid Fiber Reinforced Hybrid Composite

Investigation of the mechanical and ballistic properties of hybrid carbon/ aramid woven laminates

Experiment Study of Basalt Fiber/steel Hybrid Laminates under High-Velocity Impact Performance by Projectiles

Low-speed Impact of Glass/kevlar Hybrid Composites: Experimental Results and Numerical Verification

Investigation of Two Finite Element Modelling Approaches for Ballistic Impact Response of Composite Laminates

Experimental Study on High-velocity Impact Damage Behavior of Carbon Fiber Reinforced Composite Laminates

Study on impact properties of carbon/kevlar fiber hybrid composites

Experimental and Numerical Analysis of Ballistic Impact Response of Fiber-Reinforced Composite/metal Composite Target

Impact Response of Carbon/Kevlar Hybrid 3D Woven Composite under High Velocity Impact: Experimental and Numerical Study

Experimental and numerical investigations on the dynamic response of woven carbon fiber reinforced thick composite laminates under low-velocity impact

A STUDY ON THE FAILURE MECHANISMS OF COMPOSITE LAMINATES SIMULTANEOUSLY IMPACTED BY TWO PROJECTILES

Influence of Fabric Structure of Aramid-Reinforced Polycarbonate Composites on Its Ballistic Resistance Verified by Experiment and Simulation

High‐velocity impact resistance and energy absorption behavior of Carbon‐Kevlar hybrid composite laminates

A combined experimental/numerical study on the scaling of impact strength and toughness in composite laminates for ballistic applications