Thermostamping Experimental Study on Carbon Fiber Composite Sheet

张琦,高强,赵升吨,孙振宇

DOI: https://doi.org/10.3901/jme.2012.18.072

2011-01-01

Abstract:In order to improve the manufacturing efficiency and reduce the cost for composite parts formed by traditional composite forming processes, a thermal stamping method was proposed to directly form a composite part. The deformation region of the composite sheet was heated to a certain temperature with the locally heated die. Because the resin became softening after heating to a certain temperature, the heated sheet was formed gradually following the die movement, and then solidified in the cooling die. Thermal bending experiments of a group of ＂V＂ shape composite parts were done and the effect of process parameters, including forming temperature, loading speed, and die unloading temperature, on shape precision of formed work piece was analyzed. Thermal bending experimental results show that carbon fiber composite sheets have good bending perform ance, and the bending force is small. Recovery angle of formed workpiece at room temperature is highly related to forming parameters, which increases with the decreasing of die temperature and decreases with the decreasing of die unloading temperature.