Abstract:SummaryA novel carborane acrylate monomer (1‐acryloyloxyethyl carborane) was synthesized by addition reaction, hydrolysis, and esterification and characterized by proton nuclear magnetic resonance (1H NMR) spectroscopy and Fourier transform infrared spectroscopy (FT‐IR) analysis. Subsequently, the carborane monomer and a phosphate‐containing methacrylate monomer were applied on the modification of a silk fabric. The heat resistance and flame retardancy of the silk fabric before and after modification were compared. Energy‐dispersive X‐ray spectrometer (EDS) and FT‐IR showed that carborane monomer and phosphate‐containing methacrylate were grafted onto the surface of the fibers. The cross‐sectional morphology of silk fabrics after burning was observed by scanning electron microscope (SEM), and the flame‐retardant mechanism was analyzed. Thermal‐gravimetric analysis (TGA) and differential scanning calorimetry (DSC) analysis revealed that the thermal stability of the modified silk increased with the increase of the grafting yield. The MCC‐2 microcalorimeter (MCC) test showed that, when using 1‐acryloyloxyethyl carborane as monomer and blending with phosphate‐containing methacrylate, the maximum heat release rate (PHRR) of the modified silk fabric decreased from 97.6 W/g (before grafting) to 51.3 and 45.8 W/g, respectively, and the total heat release (THR) decreased from 10.2 kJ/g (before grafting) to 5.9 and 5.2 kJ/g, respectively. The limiting oxygen index (LOI) test revealed that using 1‐acryloyloxyethyl carborane and phosphate‐containing methacrylate as mixed monomers to modify the silk fabric obtained good flame retardancy, whose LOI value reached 29.8%.

Graft Modification on Silk with Carborane Methacrvlate

Modification of Silk Fiber Via Emulsion Graft Copolymerization with Fluoroacrylate

Synthesis of borane-silicon containing acrylate and grafting modification on silk fabrics

Technological Conditions of Silk Grafting Modification Using Atom Transfer Radical Polymerization Method

Surface Grafting Modification of Silk Fibroin by Atom Transfer Radical Polymerization

Synthesis of Boron-containing Siloxane Acrylate and Graft Modification Application on Silk Fabrics

Graft Modification of Silk Using Hexafluorobutyl Mathacrylate

Grafting of 2-Hydroxyethyl Methacrylate onto Silk by Atom Transfer Radical Polymerization

Graft Modification of N, N/-methylene- bisacrylamide onto Silk in the Presence of Air

Surface Grafting Modification of Silk Fibroin via ARGET ATRP Method

Synthesis of Octafluoropentyl Methyl Acrylate and Its Grafting Modification on Silk

Structure And Properties Of Silk Fibroin Grafted With Dimethylaminoethyl Methacrylate By Atrp In Water Aqueous

Structures of Silk Fibers Grafted with Hexafluorobutyl Methacrylate

Synthesis of Carborane Acrylate and Flame Retardant Modification on Silk Fabric Via Graft Copolymerization with Phosphate‐containing Acrylate

Study on the Grafting of HEMA on Silk Surface Via ATRP Method

Structure and Properties of Silk Grafted with N,N-Dimethylaminoethyl Methacrylate by ATRP

Structure and Hydrophobicity of Silk Fabric Grafted with Octafluoropentyl Methyl Acrylate

Structure and Properties of Silk Grafted with 2-Hydroxyethyl Methacrylate by ARGET ATRP

Surface-Initiated Atrip On Silk Fibroin In Water Aqueous At Ambient Temperature

Structure and Properties of Silk Grafted with Acrylate Fluoride Monomers by ATRP

Grafting of Methyl Methacrylate Onto Antheraea Pernyi Silk Fiber with the Assistance of Supercritical CO2