Abstract:In order to develop multi-functional silk materials, silk was grafted using the first flame retardant monomer, dimethyl methacryloyloxyethyl phosphate (DMMEP), and the second antibacterial monomer, dimethylaminoethyl methacrylate (DMAEMA), via atom transfer radical polymerization (ATRP) method. The result of attenuated total reflection-Fourier transformed infrared spectroscopy (ATR-FTIR) indicated that two monomers were successfully grafted onto silk surface. X-ray diffraction (XRD) curves showed that grafting mainly occurred at the amorphous region of silk fibers. Thermal gravimetric analysis (TGA) and flame retardance measurements indicated that the Silk-grafted-poly(DMMEP) (Silk-g-PDMMEP) and Silk-grafted-poly(DMMEP)-blocked-poly(DMAEMA) (Silk-g-PDMMEP-b-PDMAEMA) both had good flame retardance. The LOI value could reach 31.2% and the char length was less than 6cm for the Silk-g-PDMMEP sample with 22.21% of grafting percentage, and the LOI value was still over 28% after 50 times of washing. And the second grafts of DMAEMA monomer had no distinct effect on the flame retardance of Silk-g-PDMMEP. The inhibition rates of quaternized grafted silk to Staphylococcus aureu and Escherichia coli were both over 88%, and had excellent washing fastness. Multi-functional silk fabric with good flame retardance and anti-bacterial property could be obtained by properly controlling the grafting percentage, which had little effect on the intrinsic properties of silk fabric.

Grafting of 2-Hydroxyethyl Methacrylate onto Silk by Atom Transfer Radical Polymerization

Study on the Grafting of HEMA on Silk Surface Via ATRP Method

Structure and Properties of Silk Grafted with 2-Hydroxyethyl Methacrylate by ARGET ATRP

Structure and Properties of Silk Grafted with N,N-Dimethylaminoethyl Methacrylate by ATRP

Surface Grafting Modification of Silk Fibroin by Atom Transfer Radical Polymerization

Grafting of 2-Diethylaminoethyl Methacrylate Onto Silk by ATRP

Surface Grafting Modification of Silk Fibroin via ARGET ATRP Method

Surface-Initiated Atrip On Silk Fibroin In Water Aqueous At Ambient Temperature

Technological Conditions of Silk Grafting Modification Using Atom Transfer Radical Polymerization Method

Preparation, Structure, and Properties of Silk Fabric Grafted with 2-Hydroxypropyl Methacrylate Using the HRP Biocatalyzed ATRP Method

Preparation of Radical Polymerization-Grafted Silk by ATRP Method and the Structure and Properties Thereof

Surface modification of silk fabric via AGET ATRP mediated by iron catalyst

Structure And Properties Of Silk Fibroin Grafted With Dimethylaminoethyl Methacrylate By Atrp In Water Aqueous

Graft Modification on Silk with Carborane Methacrvlate

Modification of Silk Fiber Via Emulsion Graft Copolymerization with Fluoroacrylate

Synthesis of Boron-containing Siloxane Acrylate and Graft Modification Application on Silk Fabrics

Synthesis and characterization of silk fibroin/acrylic acid/acrylamide superabsorbent polymer

Structure and Properties of Silk Grafted with Acrylate Fluoride Monomers by ATRP

Preparation Technology of Grafting HEMA on Silk and Performance Estimation of Weighted Silk

Preparation, Structure and Properties of Multi-Functional Silk Via ATRP Method

Structure and Properties of Silk Grafted with N, N-Dimethylaminoethyl Methacrylate Via the Arget Atrp Method