Abstract:Electrochromic WO3 films with size controlled nanorods were successfully fabricated by a wet chemistry method. The structure and electrochromic properties of tungsten oxide nanorods and films were studied by High resolution transmission electron microscope, Scanning electron microscope, X-ray photoelectron spectroscopy, X-ray diffraction, and electrochemical methods. The average length and diameter of the monodispersed tungsten oxide nanorods increase from 38 x 3.2 nm to 89 x 4.5 nm with help from surfactants. The results show that the electrochromic response time of WO3 nanorod films are strongly dependent on the size of the nanorods. By simply changing the size of the nanorods, the response time of the nanorod films can be regulated nearly by about five times. The electrochemical impedance spectroscopy study showed that such trend can be attributed to the size effect of WO3 nanorods upon the dynamics of H ions diffusion. At the same time, all the nanorod films showed good electrochemical stability as there were no significant performance declines after 1000 cycles. The electrochromic modulations of transmittance at 633 nm were around 22%-49%. The above stated results demonstrate that, by controlling the size of WO3 nanorods, the electrochromic properties can be easily adjusted, especially the response time, indicating potential values for different response time required at different occasions. (c) 2017 Elsevier Ltd. All rights reserved.

Gasochromic Effect and Relative Mechanism of WO3nanowire Films

Synthetic and Effect of Annealing on the Luminescent Properties of Zno Nanowire

Electrochromic Properties Of Wo3 Nanowire Films And Mechanism Responsible For The Near Infrared Absorption

Evidence Of Localized Water Molecules And Their Role In The Gasochromic Effect Of Wo3 Nanowire Films

A review on WO3 gasochromic film: Mechanism, preparation and properties

Optical Characterization of the Coloration Process in Electrochromic Amorphous and Crystalline Wo3 Films by Spectroscopic Ellipsometry

Improved Electrochromic Performance of WO3 Films with Size Controlled Nanorods

Study Of Self-Heating Phenomenon And Its Resultant Effect On Ultrafast Gasochromic Coloration Of Pt-Wo3 Nanowire Films

Controllable synthesis of hexagonal WO<sub>3</sub> nanorod-cluster films with high electrochromic performance in NIR range

Xultraviolet-Visible Emission From Three-Dimensional Wo3-X Nanowire Networks

Improvement of Electrochromic Performance by Embedding ITO Nanocrystals in Amorphous WO3 Film

WO3 nanowires on carbon papers: electronic transport, improved ultraviolet-light photodetectors and excellent field emitters

Novel route to WOx nanorods and WS2 nanotubes from WS2 inorganic fullerenes.

Building Architecture of TiO2 Nanocrystals Embedded in Amorphous WO3 Films with Improved Electrochromic Properties

Novel Route to WO<i><sub>x</sub></i>Nanorods and WS<sub>2</sub>Nanotubes from WS<sub>2</sub>Inorganic Fullerenes

Effect of the Co-doping on the electrochromic performance of hexagonal phase WO3 nanorods

Electrochromic Behavior of Wo3 Nanotree Films Prepared by Hydrothermal Oxidation

Structure Design and Performance Research of WO 3 Hydrogen Gasochromic Film Prepared by Solvothermal Synthesis Assisted with Electrodeposition of Seed Layer

Field-Emission Properties of Nanostructured Wo3 Arrays Fabricated Using Tungsten Hot-Filament Chemical Vapor Deposition

Electrochemical Characteristics of Reconstructed WO3 Electrodes by Embedding ITO Nanocrystals

Plasma Assisted Pulsed Laser Deposition of WO3 Films for Thermochromism