A Facile One-Pot Route to Fabricate Nanoporous Copper with Controlled Hierarchical Pore Size Distributions Through Chemical Dealloying of Al–Cu Alloy in an Alkaline Solution
W. B. Liu,S. C. Zhang,N. Li,J. W. Zheng,Y. L. Xing
DOI: https://doi.org/10.1016/j.micromeso.2010.10.003
IF: 5.876
2011-01-01
Microporous and Mesoporous Materials
Abstract:We present a facile and effective one-pot strategy to synthesize nanoporous copper (NPC) with controlled hierarchical pore size distributions which can be fabricated through chemical dealloying of the melt-spun Al-35Cu alloy in a 10wt.% sodium hydroxide (NaOH) solution at an elevated temperature. These NPC ribbons are composed of large-sized ligament–pore structures (several hundred nanometers) at outer layers coupled with small-sized those (several ten nanometers) at inner layers. Both large- and small-sized pores are 3D, open and bicontinuous. The formation of the novel NPC ribbons can be well explained based upon the synergetic action between diffusion mechanism and pore size effect. According to the ligament sizes, the surface diffusivities at inner and outer layers of Cu adatoms can be evaluated as 3.80×10−20, 1.63×10−18, 3.54×10−18, 6.83×10−18 and 7.88×10−20, 5.41×10−17, 4.36×10−16, 4.27×10−15m2s−1 for the dealloying at 298, 333, 348 and 363K, respectively. The activation energies and diffusion constants at inner and outer layers are also measured as 47.7kJmol−1, 1.41×10−17m2s−1 and 145.3kJmol−1, 4.21×10−14m2s−1, suggesting the existence of a complicated dealloying mechanism. Additionally, the length scales of ligaments/pores at inner and outer layers can be modulated by simply changing the dealloying temperature or duration at a fixed elevated temperature.