Abstract:TiO2-diatomite photocatalysts were prepared by sol-gel process with various pre-modified diatomite. In order to obtain diatomite with different surface characteristics, two modification approaches including calcination and phosphoric acid treatment on the micro-structure of diatomite are introduced. The photocatalysts were characterized by XRD, XPS, nitrogen adsorption-desorption isotherms and micromorphology analysis. The results indicate that, compared with pure TiO2, the anatase-to-rutile phase transition temperature of TiO2 loaded on diatomite carrier is significantly increased to nearly 900 degrees C, depending on the different pretreatment method of diatomite. The photocatalytic activities of different samples were evaluated by their degradation rate of methyl orange ( MO) dye under UV and visible-light irradiation. The samples prepared by phosphoric acid pretreatment method exhibit the highest photocatalytic activity. After 90 min of UV irradiation, about 90% of MO is decomposed by the best effective photocatalyst. And after 8 h visible-light irradiation, nearly 60% of MO is decomposed by the same sample. Further mechanism investigation reveals that the H3PO4 pretreatment process can obviously change the surface features of diatomite carrier, cause the formation of Si-O-Ti bond, increase the binding strength between TiO2 and diatomite, restrain crystal growth of loaded TiO2, and thus form thermal-stable meso-porous structure at the granular spaces. It helps to build micro-, meso- and macro-porous hierarchical porous structure in TiO2-diatomite, and improves the charge and mass transfer efficiency during catalyzing process, resulting in the significantly increased photocatalytic activity of TiO2-diatomite pretreated by phosphoric acid. (C) 2014 Elsevier B. V. All rights reserved.

Preparation of Fe3+-doped TiO2 catalysts by controlled hydrolysis of titanium alkoxide and study on their photocatalytic activity for methyl orange degradation.

Influence of Fe2o3 Doping on Morphology and Photocatalytic Activity of Tio2 Prepared by Adsorption Phase Synthesis

Preparation of TiO_2/SiO_2 and Photo-Catalytic Degradation of Methyl-Orange

The Catalytic Degradation Performance of Α-Feooh Doped with Silicon on Methyl Orange

Preparation and Photocatalytic Properties of Fe(III)-Grafted TiO<sub>2</sub> Nano-Composite Powders

TiO2 Nanoparticles Supported on PMMA Nanofibers for Photocatalytic Degradation of Methyl Orange

Preparation Of Fe3+-Doped Tio2 Nanoparticles And Their Photocatalytic Activities

Preparation, Characterization and Electronic Structures of Fe-doped TiO2 Nanostructured Fibers

Preparation of Er3+:YAlO3/Fe-doped TiO2–ZnO and its application in photocatalytic degradation of dyes under solar light irradiation

Photo-catalytic activity of Fe3+/Sn4+ co-doped titanium dioxide nano-crystalline thin films for methyl orange degradation

Photodegradation of an Azo Dye Using Immobilized Nanoparticles of TiO2 Supported by Natural Porous Mineral.

Photocatalytic Degradation of Methyl Orange by Using Different Shape-controlled TiO2 Micro-crystals

Interface Actions Between TiO2 and Porous Diatomite on the Structure and Photocatalytic Activity of TiO2-diatomite

Preparation of silicon-doped TiO2 fiber and supported TiO2 and comparison study of their photocatalytic activity

Preparation of Fe3+ Doped High-Ordered TiO2 Nanotubes Arrays with Visible Photocatalytic Activities

Photo-Catalytic Activity of Fe3+/Sn4+Co-Doped Titanium Dioxide Nano-Crystalline Thin Films for Methyl Orange Degradation

Nanocrystalline Fe/TiO2 Visible Photocatalyst with a Mesoporous Structure Prepared via a Nonhydrolytic Sol-Gel Route

Enhanced Photocatalytic Degradation of Methyl Orange by Metal‐Tio2 Nanoparticles

Direct Hydro-Alcohol Thermal Synthesis of Special Core–shell Structured Fe-doped Titania Microspheres with Extended Visible Light Response and Enhanced Photoactivity

Preparation and Photocatalytic Properties of Mo-doped TiO2

One Step Preparation of Visible-Light Responsive Fe–TiO2 Coating Photocatalysts by MOCVD