Abstract:AIM: To observe the effect of the nano-surface on titanium alloy on the adhesion of osteoblasts. METHODS: The experiment was carried out from June 2004 to January 2005 in the laboratory of the Sixth People's Hospital of Shanghai city. After the osteoblasts of SD rats were primarily cultured, three methods were adopted to identify them. Inverted phase contrast microscope (IPM) was used to observe the cellular morphology. Alkaline phosphatase (ALP) staining of osteoblast and ambramycin staining of ossified nodule were also used. Golden mineralized nodule was observed under fluorescent microscope. Then osteoblasts were cultured with three different titanium alloys including smooth (S), rough(R) and nano-surface (N). The adhesive osteoblasts were counted with computer and observed with scanning electron microscope (SEM). RESULTS:① Characters of material surface: The three surfaces have different appearances under SEM. The S group was very smooth except some marks. The R group had bigger irregular fluctuation, which formed micrometer-grade pores. While N group had smaller regulated micrometer-grade pores in which there were nanometer-grade pores. ②Culture and identification of osteoblasts: Observation under inverted phase contrast showed that one or two days after inoculated bone tissue pieces attached to the wall, few shuttle and triangle cells dissociated. With the elongation of culture time, the cells at the edge of bone pieces increased and migrated to the wall of the bottle. About 2 weeks later, a unilaminar cells formed at the bottom of culture flask, presenting cluster-shape. Ungenerative cells presented more-layer shape 3 to 4 weeks later. At the center, cells gathered, calcified and formed scattered white-spot thing seen by naked eyes. ③Acridine orange staining , counting and analysis: With the elongation of time , the cells adhered on the three materials increased obviously (P < 0.01). At the same time period of 1, 2 and 4 hours, the adhered osteoblasts number was nanometer > rough > smooth in order (P > 0.01), significant difference existed in SNK test. Thus it can be seen that osteoblasts got early adhesion on the nano-surface titanium alloy. ④ Observation under electron microscope : After osteoblasts were co-cultured with materials for one hour , the number of osteoblasts on the 3 titanium alloys was nanometer > rough> smooth in oroler. Most of the cells on the nano-surface titanium alloy expanded with many mutations, while the osteoblasts on the smooth and rough surface still presented neurosphere-like shape, without extension. It was also found that osteoblasts on the rough and nano-surface titanium alloy inclined to adhere to the interface of the materials. CONCLUSION: The earlier adhesion of osteoblast can be promoted by nanotechnology. The nano-surface technology can give the advantage of nanobiology to the material maintaining the biomechanical character.

Effects of Hydrophilic Titanium Surface on the Early Adhesion of Osteoblasts

Osteogenesis of Rat Mesenchymal Stem Cells and Osteoblastic Cells on Strontium-Doped Nanohydroxyapatite-Coated Titanium Surfaces.

Effect of Hydrophilic Titanium Surface on the Proliferation and Differentiation of Osteoblasts

The influence of surface energy on early adherent events of osteoblast on titanium substrates.

Enhanced initial adhesion of osteoblast-like cells on an anatase-structured titania surface formed by H2O2/HCl solution and heat treatment

Cell Response of Titanium Implant with a Roughened Surface Containing Titanium Hydride: an in Vitro Study

Surface Modification And Its Effect On Attachment, Spreading, And Proliferation Of Human Gingival Fibroblasts

Effect of the nano-surface of titanium alloy on the adhesion of osteoblasts

The Effects of Sanding Acid Etch Treatment of Ti-6Al-7Nb Surface on Rat Osteoblasts

Enhanced Initial Proliferation and Differentiation of MC3T3-E1 Cells on HF/HNO3 Solution Treated Nanostructural Titanium Surface.

Biological and Biomechanical Behavior of Titanium Implants with Fluoridated Hydroxyapatite Coatings

Effects of Titanium Micro-Nanopermeable Structures on Osteogenic Differentiation

Effects of fluid shear stress on expression of focal adhesion kinase in MG-63 human osteoblast-like cells on different surface modification of titanium

Studying the Biocompatibility of Implant Titanium Alloy after Surface Treatment by Sandblasting and Etching

Characterization of titanium surfaces with calcium and phosphate and osteoblast adhesion.

Enhanced Bioactivity of Sandblasted and Acid-Etched Titanium Surfaces

Effect of focal adhesion kinase inhibition on osteoblastic cells grown on titanium with different topographies

The influence of titanium surfaces treated by alkalis on macrophage and osteoblast-like cell adhesion and gene expression in vitro

Influence of titanium surface hydrophobicity pattern on the growth of osteoblasts

Improvement of the Adhesion and Proliferation of Human Osteoblastic-Like Cells with Biomimetic Nanoapatite Coatings

Effects of TCP/HA-coating Titanium on the Adhesion Behavior of Human Gingival Fibroblasts