Abstract:We report the controlled hydrothermal growth of rutile TiO2 nanorods on Si wafers by using an anatase TiO2 nanodot film as an assisted growth layer. The anatase nanodot film was prepared on the wafer by phase-separation-induced self-assembly and subsequent heat-treatment at 500°C. The nanodots on the wafer were then subjected to hydrothermal treatment to induce the growth of rutile TiO2 nanorod films. The size and dispersion density of the resulting TiO2 nanorods could be varied by adjusting the Ti ion concentration in the growth solution. The TiO2 nanorods were of the rutile phase and grew in the [001] direction. The growth mechanism reveals that the growth of the rutile nanorods was wholly dependent on the existence of rutile TiO2 seeds, which could be formed by the dissolution–reprecipitation of the anatase nanodots during hydrothermal treatment or under the high-temperature conditions of the subsequent heat-treatment of the as-prepared nanodots. In controlling the rutile nanorod growth, the anatase nanodots show more efficiency than a dense anatase film. Preliminary evaluations of the rutile nanorod films have demonstrated that the wettability changed from highly hydrophobic to superhydrophilic and that the photocatalytic activity was enhanced with increasing nanorod dispersion density.

Facile fabrication of rutile monolayer films consisting of well crystalline nanorods by following an IL-assisted hydrothermal route

Low‐Temperature Growth of Rutile Nanorod Thin Films and Their Photon‐Induced Property

Low‐Temperature Growth of Monolayer Rutile TiO2 Nanorod Films

Tio2 Nanorod Films Grown on Si Wafers by A Nanodot-Assisted Hydrothermal Growth

Growth of rutile TiO 2 nanorods on anatase TiO 2 thin films on Si-based substrates

Hydrothermal Growth of Rutile Tio2 Nanorod Films on Titanium Substrates

Effects of Hydrothermal Time on the Morphologies of Rutile TiO2 Hierarchical Nanoarrays and Their Optical and Photocatalytic Properties

Rapid-Heating-Triggered in Situ Solid-State Transformation of Amorphous TiO2 Nanotubes into Well-Defined Anatase Nanocrystals

Fabrication of Well-Aligned Tio2 Nanotube Arrays with Outstanding Light-Induced Hydrophilicity Performance

Ordered Mesoporous Thin Films Of Rutile Tio2 Nanocrystals Mixed With Amorphous Ta2o5

Large-scale Synthesis and Characterization of Fan-Shaped Rutile TiO2 Nanostructures

Pulsed Laser Deposition of Titania on Rutile Nanorod Arrays

Direct Deposition of A Rutile Layer on Polymer Substrates to Induce Bioactivity in Vitro

Mesocrystals Of Rutile Tio2: Mesoscale Transformation, Crystallization, And Growth By A Biologic Molecules-Assisted Hydrothermal Process

Preparation and photodegradation activity of high aspect ratio rutile TiO2 single crystal nanorods

Ligand-Free Self-Assembly Of Ceria Nanocrystals Into Nanorods By Oriented Attachment At Low Temperature

Large-Scale Preparation Of Ordered Titania Nanorods With Enhanced Photocatalytic Activity

Photoelectrocatalytic Efficiency of Low-Temperature Precipitated Monolayer Rutile TiO 2 Nanoflower Film

Low-temperature preparation of titania nanorods through direct oxidation of titanium with hydrogen peroxide

MICROWAVE HYDROTHERMAL SYNTHESIS OF RUTILE <font>TiO</font><sub>2</sub> NANORODS

Microwave Hydrothermal Synthesis Of Rutile Tio2 Nanorods