Remarkably improved interfacial adhesion of UHMWPE fibers reinforced composite by constructing a three-dimensional stacked nanoparticles structure at interphase
Kui Wang,Lu Shen,Rong Lu,Zhao Yang,Zongbao Qin
DOI: https://doi.org/10.1016/j.jiec.2022.03.031
IF: 6.76
2022-03-01
Journal of Industrial and Engineering Chemistry
Abstract:Highlights•A unique biomimetic layer, which exhibited a three-dimensional stacked nanoparticles structure, was prepared by the synergistic effect of PDA and APTES via a mild and convenient process.•The unique stacked nanoparticles structure made fibers surface possess high surface roughness, high surface energy and improved wettability.•The IFSS of modified fibers exhibited an extraordinary 407.8 % increase (8.36 MPa) relative to untreated UHMWPE (2.05 MPa).•Owing to the unique structure on modified fibers surface, the crack transmitting path became longer and more complicated.•The failure mechanism of the fibers with the highest IFSS transformed from adhesive failure to both cohesive failure and substrate failure.Ultrahigh molecular weight polyethylene (UHMWPE) fibers have an ultralow interfacial property because of their extraordinarily smooth and nonpolar surfaces, and this property is a persistent problem in UHMWPE fiber-reinforced composites. In this investigation, a novel one-step and mild strategy for enhancing the interfacial property of UHMWPE fiber-reinforced composites was reported. In this strategy, a biomimetic layer with abundant stacked and three-dimensional nanoparticles formed on fibers surface through the synergistic effect of polydopamine and 3-aminopropyltriethoxysilane. Owing to the unique three-dimensional structure and sufficient polar groups on the fibers surface, surface roughness and surface energy significantly increased, and wettability improved. Consequently, the interfacial shear strength (IFSS) of the fibers exhibited a 407.8% increase (8.36 MPa) relative to that of untreated UHMWPE (2.05 MPa) because of these synergistic effects. Further analysis indicated that the failure mechanism of the fibers with the highest IFSS was the transformation from adhesive failure to cohesive failure and substrate failure. The mild preparation process maintained the high crystallinity and orientation of the modified UHMWPE fibers, which exhibited a high tensile force of up to 81 cN.Graphical abstractDownload : Download high-res image (105KB)Download : Download full-size image
engineering, chemical,chemistry, multidisciplinary