Abstract:Hollow titania microparticles about 20-60 mu m in size and hollow titania/carbon composite microparticles about 30-90 mu m in size were prepared by employing commercial Sephadex G-100 beads as the template as well as the carbon precursor. The cross-linked dextran gel template was first immersed in aqueous TiCl4 solution to allow the surface mineralization of titania, resulting in the formation of hollow microparticles of titania/G-100 hybrids. Hollow titania microparticles with a shell thickness adjustable from 1 mu m to 2.5 mu m were fabricated by calcination of the hollow titania/G-100 hybrid microparticles at temperatures from 400 to 700 degrees C in air. On the other hand, hollow titania/carbon composite microparticles similar to 2.6 mu m in shell thickness, which consisted of anatase nanocrystals and amorphous carbon, were obtained by carbonization of the hollow titania/G-100 hybrid microparticles at temperatures from 500 to 700 degrees C in flowing nitrogen. For the titania/carbon composites, the phase transformation from anatase to rutile was suppressed; moreover, the crystallinity of anatase was decreased and the surface area was increased with increasing calcination temperature, in contrast to the case of hollow titania microparticles. The photocatalytic activity of the obtained hollow microparticles of titania and titania/carbon composites was investigated by monitoring the photodegradation of Rhodamine B. In both cases, the product calcined at an intermediate temperature exhibited the highest photocatalytic activity possibly because of a compromise between the anatase crystallinity and the surface area. Compared with the hollow titania microparticles, the hollow titania/carbon composite microparticles exhibit remarkably enhanced photocatalytic activity.

Synthesis of Mesoporous Titania Networks Consisting of Anatase Nanowires by Templating of Bacterial Cellulose Membranes

Synthesis of ordered mesoporous crystalline carbon-anatase composites with high titania contents.

Synthesis of hierarchical mesoporous titania with interwoven networks by eggshell membrane directed sol–gel technique

Fabrication and Photocatalytic Activity of Tio2 Nanofiber Membrane

Biomimetic Nanoarchitectonics: Natural Cellulose Based Nanocomposites As High Performance Catalysts

Tubular Structured Hierarchical Mesoporous Titania Material Derived from Natural Cellulosic Substances and Application As Photocatalyst for Degradation of Methylene Blue

Hierarchical Mesoporous Silica Nanotubes Derived from Natural Cellulose Substance.

Titania nanotube/hollow sphere hybrid material: Dual-template synthesis and photocatalytic property

Synthesis of Mesoporous Titania with High Photocatalytic Activity by Nanocrystalline Particle Assembly

Hydrothermal Synthesis and Morphological Evolution of Mesoporous Titania−Silica

Templated Synthesis of TiO2 Nanotube Macrostructures and Their Photocatalytic Properties

Synthesis and Characterizations of Hierarchical Biomorphic Titania Oxide by A Bio-Inspired Bottom-Up Assembly Solution Technique

Three-dimensional Interconnected Mesoporous Anatase TiO2 Exhibiting Unique Photocatalytic Performances

Heterogeneous nanotubular anatase/rutile titania composite derived from natural cellulose substance and its photocatalytic property

Hierarchical-structured anatase-titania/cellulose composite sheet with high photocatalytic performance and antibacterial activity.

Novel Approach for the Synthesis of Nanocrystalline Anatase Titania and Their Photovoltaic Application

Porous TiO2 Nanowires Derived from Nanotubes: Synthesis, Characterzation and Their Enhanced Photocatalytic Properties

Mesoporous titanium dioxide (TiO2) with hierarchically 3D dendrimeric architectures: formation mechanism and highly enhanced photocatalytic activity.

Single‐Crystal‐like Titania Mesocages

Synthesis of Titania Nanocubes Induced by Cellulose Nanocrystal and Its Photocatalytic Properties

Synthesis and Photocatalytic Properties of Hollow Microparticles of Titania and Titania/Carbon Composites Templated by Sephadex G-100